Abstract: Promising capacity retention (more than 92% of initial capacity after 100cycles), was exhibited in cells (graphite/xLi2MnO3·yLiMO2) with 2wt.% LiDFOB as additive. The outstanding cell performance was associated with the formation of stable solid electrolyte interface (SEI) film on the surface of electrodes derived from LiDFOB. Compared to the effect of the LiBOB additive, the main reason responsible for the greatly improved durability in LiDFOB added cells might be attributed to the more stable SEI film with lower interfacial resistance on the surface of anode. [Copyright &y& Elsevier]

Abstract: A novel C/Co composite with Co nanoparticles embedded in carbon matrix is synthesized firstly by pyrolysis of polymeric cobalt phthalocyanine (PcCo) at 700°C in argon atmosphere. This composite is investigated as an anode material for lithium ion batteries, indicating high tap density and excellent electrochemical performance. The C/Co electrode can retain a higher reversible capacity of over 600mAhg−1 at a current of 50mAg−1 after 40cycles and shows better rate capability and less hysteresis in comparison to carbon not containing Co. The significant improvement is attributed to the Co nanoparticles grown in-situ reaction with catalytic activity and high electrical conductivity. [Copyright &y& Elsevier]

Abstract: A unique ordered mesoporous Sn–C composite with Sn nanoparticles confined in carbon nanorods was prepared using SBA-15 as the template. This composite was employed as the anode material of Li-ion batteries, delivering excellent electrochemical properties of high reversible lithium storage capacity (554 mAh g−1 after 200 cycles) and great rate capability (as high as 5000mA g−1). [Copyright &y& Elsevier]

Abstract: In this paper, flower-like spinel Li4Ti5O12 consisting of nanosheets was synthesized by a hydrothermal process in glycol solution and following calcination. The as-prepared product was characterized by scanning electron microscopy, transmission electron microscopy, X-ray powder diffraction and cyclic voltammetry. The capacity of the sample used as anode material for lithium ion battery was measured. This structured Li4Ti5O12 exhibited a high reversible capacity and an excellent rate capability of 165.8mAhg−1 at 8C, indicating potential application for lithium ion batteries with high rate performance and high capacity. [Copyright &y& Elsevier]

Abstract: This work reports the facile synthesis of an amorphous FePO4 hollow nanosphere with tunable shell thickness for use as a cathode material in lithium ion batteries (LIBs). This material exhibits good electrochemical performance with a high specific capacity, a high rate capability, and good capacity retention upon cycling. [Copyright &y& Elsevier]