Abstract: Continuous nanocrystalline diamond (NCD) films were grown in an argon-rich gas atmosphere with relatively high growth rates by sustaining a low power (5 W) DC plasma in a hot filament chemical vapor deposition system (HFCVD). The parameter window for the synthesis of NCD films was studied as a function of argon, methane and hydrogen concentrations, as well as substrate temperature and DC bias. The results are consistent with reports indicating that the DC plasma induces re-nucleation by ion bombardment during the initial growth step and helps to maintain the atomic H and hydrocarbon species near the growing surface. It was found that DC plasma-assisted HFCVD enables high NCD growth rates and expands the parameter window, rendering it unnecessary to heat the filament above 2800 K. [Copyright &y& Elsevier]

Abstract: Sulfur-assisted hot-filament chemical vapor deposition (HFCVD) was recently employed to grow diamond nano-crystals on polyimide film [F. Piazza, G. Morell, Diamond and Related Materials, 16 (2007) 1950], unambiguously showing that the substrate temperature was below 360 °C, the polyimide glass transition temperature. This accomplishment has opened the door to employ diamond in a wide range of applications where it needs to be integrated with temperature sensitive materials. The result reported earlier relies on visible Raman spectroscopy analysis. We hereby report new additional evidences confirming the result from transmission electron microscopy (TEM), high-resolution TEM, energy dispersive X-ray analysis, electron energy loss spectroscopy and selected area electron diffraction. [Copyright &y& Elsevier]

Abstract: Sulfur-assisted hot-filament chemical vapor deposition was successfully employed to synthesize diamond films at relatively low substrate temperatures, sub 500 °C, on Mo and glass substrates. This result is ascribed to sulfur-containing species that create an additional carbon transport channel to the substrate, which explicitly requires a large temperature gradient to effectively operate. The grain size and roughness were found to decrease when the Mo substrate temperature was decreased, while the quality factor only showed a slight decrease. Moreover, the diamond quality, grain size, and roughness were found to increase on glass substrates in comparison to those on Mo substrates. [Copyright &y& Elsevier]