Search

Highly polished 3, 4, and 5 mol% yttria-stabilized zirconia and CAD/CAM composite resin samples were prepared, and the influence of surface roughness (Ra and Sa, 21 areas/group), wettability (contact angle and surface energy, 3 samples/group), and surface chemical composition (2 samples/group) on single-strain bacterial adhesion models (Porphyromonas gingivalis, Streptococcus oralis, Streptococcus sanguinis, Streptococcus gordonii, and Streptococcus mutans) were compared via fluorescent staining with graphical analysis (21 areas/group). Statistical analysis was performed using the Shapiro–Wilk test followed by one-way analysis of variance with Tukey’s test or the Kruskal–Wallis test with Dunn’s test (α=0.05) and linear regression. For dental zirconia with the same surface roughness, the yttria content did not significantly influence the initial bacterial adhesion. However, higher bacterial adhesion was detected for the composite resin owing to its high C, O, and Si contents. There was no correlation between surface energy and bacterial adhesion for any bacterial strain (p<0.005). [ABSTRACT FROM AUTHOR]

We aimed to elucidate the effects of ultraviolet (UV) irradiation on the shear bond strength (SBS) between heat-cured polymethyl methacrylate (PMMA) and a Co-Cr-Mo alloy. Disk-shaped Co-Cr-Mo alloy prepared by casting were subjected to different UV treatment times (0, 15, and 30 min). To determine the effect of UV treatment on surface properties of the alloy, surface roughness, wettability, and chemical compositions were analyzed. To evaluate the SBS, cylindrical PMMA was bonded to the UV-treated alloy, and subsequently subjected to the SBS test after 24 h of storage at room temperature or following 10,000 thermal cycles (n=10/group). After the UV treatment, the surface roughness remained unchanged, but oxidation resulted in the surface exhibiting greater hydrophilic characteristics. The UV-treated group showed significantly higher SBS values than those of the non-treated group (p<0.001). These results suggested that UV treatment-mediated oxidation improved the bond strength between PMMA and Co-Cr-Mo alloy. [ABSTRACT FROM AUTHOR]

There is limited research on the influence of different sintering temperatures on the properties of highly translucent zirconia ceramics. This study demonstrated the influence of different sintering temperatures on the translucency, crystallographic structure, biaxial flexural strength, microstructure, and low-temperature degradation (LTD) of three highly translucent zirconia grades, i.e., 3 mol% yttria-stabilized tetragonal zirconia polycrystals (3Y-TZP), 4 mol% yttria-partially-stabilized zirconia (4Y-PSZ), and 5 mol% yttria-PSZ (5Y-PSZ). The specimens were characterized using colorimetry, X-ray diffraction, scanning electron microscopy, Weibull analysis, and LTD tests (134°C; 20 h). The increase in the sintering temperature did not affect the translucency of 3Y-TZP, whereas it increased the translucencies of 4Y-PSZ and 5Y-PSZ. All the zirconia grades exhibited grain enlargement and unchanged biaxial flexural strengths with the increase in the sintering temperature. The degradation of 3Y-TZP and 4Y-PSZ at a sintering temperature of 1,600°C was faster than that at other sintering temperatures. [ABSTRACT FROM AUTHOR]

The influence of sulfinate agents applied as a dentin pretreatment or a mixture with multi-mode one-step self-etch adhesives (1-SEAs) on the degree of conversion (DC) and micro-tensile bond strength (μTBS) of light-cured 1-SEAs was investigated. 1-SEAs Clearfil Universal Bond Quick (UBQ) or Scotchbond Universal Adhesive (SBU) were applied to dentin in etch&rinse or self-etch mode using various application strategies: 1) no pretreatment, 2) pretreatment with 90 wt% ethanol, 3) pretreatment with a sulfinate agent Clearfil DC Activator (UDC) or Scotchbond Universal DCA (SDC), or 4) a mixture of UBQ+UDC or SBU+SDC. μTBS was measured after 24 h. Additionally, DC was measured using attenuated total reflectance Fourier-transform infrared spectroscopy. Pretreatment with sulfinate agents resulted in the highest μTBS and DC, significantly improving them especially in etch&rinse mode. The mixture of sulfinate agents with 1-SEAs was less effective. Pretreatment with ethanol significantly improved μTBS in etch&rinse mode but compromised μTBS in self-etch mode. [ABSTRACT FROM AUTHOR]

The purpose of this study was to evaluate the influence of resin-coating using one-bottle adhesives on the bond strength of resin cements in single-visit and multiple-visit treatments. Three one-bottle adhesives were used for resin-coating and/or pre-treatment adhesives prior to cementation, in conjunction with resin cements from the same manufacturers: Clearfil Universal Bond Quick with Panavia V5 (UBQ/Pv5), Scotchbond Universal Adhesive with RelyX Ultimate (SBU/RxU), and Optibond All-in-one with NX3 Nexus (OP/NX3). Bovine dentin surfaces were left uncoated or resin-coated. After 1-h water storage (single-visit) or 1-week water storage with a non-eugenol temporary cement (multiple-visit), a CAD/CAM resin block was cemented to uncoated or resin-coated dentin surfaces. Microtensile bond strengths (µTBSs) were measured and statistically analyzed (α=0.05). Application of resin-coating improved µTBSs. The multiple-visit group exhibited lower values of µTBS than the single-visit group. Selection of the materials affected µTBSs. Resin-coating and single-visit treatment are desirable for CAD/CAM resin composite restorations. [ABSTRACT FROM AUTHOR]

This study aims to elucidate the relationships between the flexural strength and surface topography of composite resin blocks, utilized for the CAD/CAM system, after milling in various step-over amounts. The rectangular specimens were milled from CAD/CAM blocks with step-over amount 0.01, 0.02, 0.05, 0.1, and 0.2 mm; further, a three-point bending test was conducted to reveal the flexural strength. The surface morphology after milling was assessed by a 3D laser microscope. The surface roughness significantly decreased by reducing the step-over amount. Although there was significant association between the surface roughness and flexural strength by the Pearson correlation, the 95% confidence intervals of the flexural strength were between the mirror-polished and sand-blasted groups. These results suggest that a precise step-over amount enables us to obtain a smooth surface. Furthermore, the flexural strength of the rough surface milled by a large step-over amount caused no damage to the composite resin for CAD/CAM crown. [ABSTRACT FROM AUTHOR]

This study investigated the efficacy of copper (Cu) as an antibacterial element incorporated on titanium (Ti) surface by electrochemical treatment. Cu was incorporated onto Ti surface by micro-arc oxidation (MAO). A small amount of Cu was incorporated into the oxide layer and was found to be in oxidized states. Cu-incorporated samples exhibited no-harmful effect on the proliferation of osteoblastlike cells. Moreover, the difference in antibacterial property between fresh and incubated samples was evaluated using gram-positive and gram-negative facultative anaerobic bacteria. The specific antibacterial property of Cu incorporated into the Ti surface were confirmed. The antibacterial property prolonged upon immersion in physiological saline for 28 days. In other words, MAO-treated Ti containing Cu in this study is expected to achieve long-term antibacterial property in practical usage. [ABSTRACT FROM AUTHOR]

In the present study, the influence of the SiO2 content of polyetheretherketone (PEEK) on the bonding between PEEK and resin cement, and the corresponding mechanical properties, were evaluated. Three experimental PEEK samples with varying amounts of SiO2, and PEEK containing 20 wt% of TiO2 (DK), were investigated. The tensile bond strength (TBS) was evaluated before and after 10,000 thermal cycles, upon polishing, sandblasting, and conditioning of the specimens with BONDMER lightless containing a silane coupling agent, and bonded with ESTECEM II. The crystallinity, flexural modulus, and flexural strength were determined after 10,000 thermal cycles. TBS values were analyzed by two-way ANOVA and a t-test with Bonferroni correction (α<0.05), while the crystallinity, flexural modulus, and flexural strength were analyzed with one-way ANOVA followed by a t-test with Bonferroni correction (α<0.05). The TBS improved with increasing SiO2 content in PEEK; moreover, DK and the sample with 40 wt% SiO2 exhibited the highest flexural strength. [ABSTRACT FROM AUTHOR]

This study investigated the surface characteristics and antibacterial ability capacity of surface-improved dental glass-ceramics by an electrical polarization process. Commercially available dental glass-ceramic materials were electrically polarized to induce surface charges in a direct current field by heating. The surface morphology, chemical composition, crystal structure, and surface free energy (SFE) were evaluated using scanning electron microscopy, energy dispersive X-ray spectrometry, X-ray diffraction, and water droplet methods, respectively. The antibacterial capacity was assessed by a bacterial adhesion te st using Streptococcus mutans. Although the surface morphology, chemical composition, and crystal structure were not affected by electrical polarization, the polar component and total SFE were enhanced. After 24 h incubation a t 37°C, bacterial adhesion to the polarized samples was inhibited. The electrical polarization method may confer antibacterial properties on prosthetic devices, such as porcelain fused to metal crowns or all ceramic restorations, without any additional bactericidal agents. [ABSTRACT FROM AUTHOR]

This study aimed to investigate the maximum depth imaging and optical properties of the dentin near the pulp by using opticalcoherence tomography (OCT) and to explore the possibility of measuring the remaining dentin thickness (RDT). Human third molarswere used. In experiment 1, the cuspal dentin blocks (0.50-mm to 1.75-mm thickness) were prepared. Each specimen was scannedusing OCT. OCT images could be obtained for all specimens with 1.00-mm or less thicknesses. In experiment 2, dentin-pulp complexslices (0.50-mm and 1.00-mm RDT) were prepared. Each specimen was scanned using OCT and micro-computed tomography, andcompared. The resulting length change rates of OCT images for the 0.50-mm RDTs were significantly lower than those of the 1.00-mm RDTs. Within the limitations of this study, OCT was effective for measuring the 1.00-mm or less RDT and preventing pulpalinjury, while considering the length change rate of OCT image as a variable. [ABSTRACT FROM AUTHOR]