We aimed to elucidate the effects of ultraviolet (UV) irradiation on the shear bond strength (SBS) between heat-cured polymethyl methacrylate (PMMA) and a Co-Cr-Mo alloy. Disk-shaped Co-Cr-Mo alloy prepared by casting were subjected to different UV treatment times (0, 15, and 30 min). To determine the effect of UV treatment on surface properties of the alloy, surface roughness, wettability, and chemical compositions were analyzed. To evaluate the SBS, cylindrical PMMA was bonded to the UV-treated alloy, and subsequently subjected to the SBS test after 24 h of storage at room temperature or following 10,000 thermal cycles (n=10/group). After the UV treatment, the surface roughness remained unchanged, but oxidation resulted in the surface exhibiting greater hydrophilic characteristics. The UV-treated group showed significantly higher SBS values than those of the non-treated group (p<0.001). These results suggested that UV treatment-mediated oxidation improved the bond strength between PMMA and Co-Cr-Mo alloy.

The artifact volume generated in magnetic resonance (MR) images was quantitatively evaluated to investigate how artifact behavior correlates to the magnetic susceptibility and volume of an implanted metal device. For this, a new low-magnetic-susceptibility Zr-14Nb alloy was compared with two conventional dental alloys, Ti-6Al-7Nb alloy and Co-Cr-Mo alloy, using spherical specimens of each alloy prepared with four different diameters. Then, MR images were recorded under fast spin echo and gradient echo conditions, from which the artifact volume was measured. The artifact volume decreased with the magnetic susceptibility, volume, and mass of the specimens, and significant linear correlations were observed. The artifact volume can be estimated by the equations presented here; nevertheless, further studies are necessary to interpret the influence of some important factors (e.g., imaging conditions, shape, and orientation) to predict the artifact volume more precisely.

The purpose of this study was to evaluate mechanical properties, surface characteristics and castability of Zr-14Nb dental castings. The mean 0.2% proof and ultimate tensile strengths of Zr-14Nb were approximately 68% and 76% those of Ti-6Al-7Nb, respectively, while they were comparable to Co-29Cr-6Mo. Elongation of Zr-14Nb was the highest of all alloys tested. The hardened reaction layer was formed on the surfaces of the Zr-14Nb castings. The layer consisted of oxygen and aluminum originating form investment. The castability of Zr-14Nb was comparable to that of Ti-6Al-7Nb. Dental castings of Zr-14Nb reveal mechanical properties that were within the range of the other dental alloys. Further improvements in castability and minimization of the surface reaction layer are needed for applications in dental prostheses.