Search

The α,α′-bis(imino)-2,3:5,6-bis(pentamethylene)pyridyl-cobalt(II) chlorides, [2,3:5,6-{C4H8C(N(2-R1-4-R3-6-R2C6H2))}2C5HN] CoCl2 (R1 = Me, R2 = R3 = CH(p-FPh)2Co1; R1 = Et, R2 = R3 = CH(p-FPh)2Co2; R1 = i-Pr, R2 = R3 = CH(p-FPh)2Co3; R1 = Cl, R2 = R3 = CH(p-FPh)2Co4; R1 = F, R2 = R3 = CH(p-FPh)2Co5; R1 = F, R2 = R3 = CHPh2Co5′′, R1 = R2 = Me, R3 = CH(p-FPh)2Co6; R1 = R3 = Me, R2 = CH(p-FPh)2Co7), have been synthesized by a one-pot template reaction of α,α′-dioxo-2,3:5,6-bis(pentamethylene)pyridine, cobalt(II) chloride and the respective aniline in n-butanol. By contrast, the mixed cobalt(II) chloride/acetate complex, [2,3:5,6-{C4H8C(N(2-F-4,6-(CH(p-FPh)2)2C6H2))}2C5HN]CoCl(OAc) (Co5′), was isolated when the corresponding template reaction was carried out in acetic acid. Structural characterization of Co4, Co5 and Co5′′ revealed distorted square pyramidal geometries while six-coordinate Co5′, incorporating a chelating acetate ligand, exhibited a distorted octahedral geometry. On activation with either MAO or MMAO, 2-fluoride-4,6-bis{di(p-fluorophenyl)methyl}-substituted Co5 showed maximum catalytic activity for ethylene polymerization at a high operating temperature of 60 °C (up to 2.1 × 107 g (PE) mol−1 (Co) h−1), producing highly linear (Tms > 121 °C), low molecular weight polyethylene waxes (Mw range: 1.5–5.0 kg mol−1) with narrow dispersity (Mw/Mn range: 1.7–2.9). End-group analysis of the waxes reveals β-H elimination as the dominant chain transfer process. [ABSTRACT FROM AUTHOR]

A one-pot template strategy has been utilized to synthesize sterically enhanced bis(imino)cyclohepta[b]pyridine-cobalt(II) chlorides, [2-{(Ar)N＝CMe}-9-{N(Ar)}C10H10N]CoCl2 (Ar = 2-(C5H9)-4,6-(CHPh2)2C6H2Co1, 2-(C6H11)-4,6-(CHPh2)2C6H2Co2, 2-(C8H15)-4,6-(CHPh2)2C6H2Co3, 2-(C12H23)-4,6-(CHPh2)2C6H2Co4, 2,6-(C5H9)2-4-(CHPh2)C6H2Co5). All five complexes have been characterized by a combination of FT-IR spectroscopy, elemental analysis and single crystal X-ray diffraction. The molecular structures of Co1, Co3 and Co5 highlight the substantial steric hindrance imparted by the 2-cycloalkyl-6-benzhydryl or 2,6-dicyclopentyl ortho-substitution pattern; distorted square pyramidal geometries are exhibited in each case. On activation with methylaluminoxane (MAO) or modified methylaluminoxane (MMAO), all the complexes (apart from Co4/MAO) were active ethylene polymerization catalysts (up to 3.70 × 106 g PE per mol (Co) per h for Co5/MMAO), operating effectively at temperatures between 50 °C and 60 °C, producing polyethylenes with high molecular weights (up to 589.5 kg mol−1 for Co3/MAO). Furthermore, all polymers were highly linear (Tm > 130 °C) with narrow dispersities (Mw/Mn range: 2.0–3.0). The coexistence of two chain termination pathways, β-H elimination and transfer to aluminum, has been demonstrated using 13C/1H NMR spectroscopy. [ABSTRACT FROM AUTHOR]

Six examples of dinuclear bis(imino)pyridine-cobalt(ii) complexes, [1,5-{2-(CMe=N)-6-(CMe=N(2,6-R12-4-R2-C6H2))C5H3N}2(C10H6)]Co2Cl4 (R1 = Me, R2 = H Co1; R1 = Et, R2 = H Co2; R1 = iPr, R2 = H Co3; R1 = Me, R2 = Me Co4; R1 = Et, R2 = Me Co5; R1 = CHPh2, R2 = Me Co6), have been prepared from the corresponding bis(tridentate) compartmental ligands (L1–L6) in reasonable yields. The molecular structures of Co3 and Co5 revealed two N,N,N-cobalt dichloride units to adopt anti-positions about the 1,5-naphthyl linking unit, with each cobalt center exhibiting a distorted trigonal bipyramidal geometry. On activation with either MAO or MMAO, Co1–Co6 were shown to promote both polymerization and oligomerization of ethylene with high overall activities (up to 1.03 × 107 gPE per·mol(Co) per·h for Co1/MAO at 70 °C). Curiously, on increasing the reaction temperature a larger proportion of polymer was noted, while at lower temperature an enhanced selectivity for oligomer was seen. In general, the oligomeric products displayed Schulz–Flory distributions with high selectivities for α-olefins (＞99%). On the other hand, the highly linear polymers displayed narrow dispersities and comprised both fully saturated and unsaturated chain ends with the vinyl content (–CH=CH2) found to rise with the reaction temperature. By modulating the steric hindrance exerted by the ortho-R1 substituents in the precatalyst, polyethylenes displaying a remarkably broad range of molecular weights could be obtained [from 4.52 kg mol−1 (R1 = Me) to 246.7 kg mol−1 (R1 = CHPh2)]. [ABSTRACT FROM AUTHOR]

A family of six unsymmetrical N,N′-diiminoacenaphthene-nickel(ii) bromide complexes, [1-{2,6-(Ph2CH)2-4-MeC6H2N}-2-(ArN)C2C10H6]NiBr2 (Ar = 2-(C6H11)-6-MeC6H2Ni1, 2-(C5H9)-6-MeC6H2Ni2, 2-(C8H15)-6-MeC6H2Ni3, 2-(C6H11)-4,6-Me2C6H2Ni4, 2-(C5H9)-4,6-Me2C6H2Ni5, 2-(C8H15)-4,6-Me2C6H2Ni6), each bearing one ring-size variable 4-R-2-methyl-6-cycloalkyl-substituted N-aryl group and one N′-4-methyl-2,6-dibenzhydrylphenyl group, have been prepared and fully characterized. The molecular structures of Ni1, Ni2, Ni3 and Ni5 reveal distorted tetrahedral geometries with different degrees of steric protection imparted by the two inequivalent N-aryl groups. On activation with either EASC or MMAO, all the precatalysts are highly active (up to 17.45 × 106 g PE mol−1 (Ni) h−1) for ethylene polymerization at 20–50 °C with their activities correlating with the type of cycloalkyl ortho-substituent: cyclooctyl (Ni6, Ni3) ＞ the cyclopentyl (Ni5, Ni2) ＞ cyclohexyl (Ni4, Ni1) for either R = H or Me. Moderately branched to hyperbranched polyethylenes (Tm's as low as 44.2 °C) can be obtained with molecular weights in the range 2.14–6.68 × 105 g mol−1 with the branching content enhanced by the temperature of the polymerization. Dynamic mechanical analysis (DMA) and monotonic tensile stress–strain tests have been employed on the polyethylene samples and reveal the more branched materials to show good elastic recovery properties (up to 75.5%). [ABSTRACT FROM AUTHOR]