Search

Introduction Zirconia is a widely used restorative material in dentistry due to its superior aesthetic and mechanical properties. The oral cavity is a complex ecosystem with various components, which affect the teeth, as well as artificial restorative materials. Various personal and professional interventions carried out can severely affect the properties of restorative materials, thus altering the longevity of the prosthesis; 1.23% acidulated phosphate fluoride (APF) gel is one such professionally applied topical fluoride agent used to prevent caries. The interaction of this APF gel with highly aesthetic restorative material such as zirconia crowns is unknown. Objective The objective of this study is the evaluation of the surface deterioration of prefabricated zirconia crowns on exposure to deionised water and 1.23% acidulated phosphate fluoride (APF) gel with field emission scanning electron microscope (FE-SEM) and mass loss analysis. Material and method Sixty prefabricated paediatric zirconia crowns were taken, 10 samples were immersed in deionised water, 40 samples were immersed in 1.23% APF gel and 10 samples were used as control. Surface morphology and mass loss analysis were carried out at time intervals of four minutes, 24 hours, 48 hours and 72 hours using FE-SEM and digital weighing machine. Results No visual change was observed in the samples immersed in deionised water at the time interval of 72 hours. There was a marked visual change in samples immersed in 1.23% APF gel at the time interval of four minutes to 72 hours; this change involved a loss of gloss to the appearance of chalkiness. FE-SEM analysis for the control group and samples immersed in deionised water showed a smooth, continuous, undisrupted top layer, while samples immersed in 1.23% APF gel showed changes ranging from surface etching, to pinhole porosities, to crack formation and disruption of the surface depending upon the exposure time. Conclusions On the immersion of zirconia crowns in an aqueous acidic medium of 1.23% APF gel, the crowns showed flaws, imperfections and uneven superficial layers. It has been observed that surface grains are disrupted and micropores have been formed. This degraded superficial surface when undergoes cyclic mechanical loading can accelerate the ageing phenomenon of zirconia. Mechanical forces along with a dynamic electrochemical environment can degrade the material properties of zirconia., Competing Interests: Human subjects: All authors have confirmed that this study did not involve human participants or tissue. Animal subjects: All authors have confirmed that this study did not involve animal subjects or tissue. Conflicts of interest: In compliance with the ICMJE uniform disclosure form, all authors declare the following: Payment/services info: All authors have declared that no financial support was received from any organization for the submitted work. Financial relationships: All authors have declared that they have no financial relationships at present or within the previous three years with any organizations that might have an interest in the submitted work. Other relationships: All authors have declared that there are no other relationships or activities that could appear to have influenced the submitted work., (Copyright © 2024, Makwana et al.)

Peri-implant disease is usually caused by the accumulation of dental biofilm around the implant, and this biofilm can irradiate the gingiva tissue, which leads to inflammation and, more severely, to a deterioration of the bone structure. There is a concern regarding the removal of biofilm from the implant surface by using different hygiene instruments. Some hygiene instruments may have some effect on the dental implant surface, resulting in roughening or damage to the implant surfaces. This study reviewed the effects of titanium implant surfaces on different hygiene instruments. A literature search was conducted from PubMed, ScienceDirect, and Scopus databases for articles published from 1992 to 2021. A total of 19 full-text papers with keywords of interest that met all the eligibility criteria were selected. Surface roughness was evaluated with a scanning electron microscope and also using a profilometer, laser scanning, scanning probe, and atomic force microscopes. A metal curette produced a roughened surface on the titanium implant, but a plastic curette did not alter the surface. Instrumentation with rubber cups left the surface unchanged and appeared to smoothen the surface, whereas the air-powder abrasive instrumentation altered the surface with the presence of micro pits and pores. A conventional metal ultrasonic scaler showed significant surface topographical changes and scratches on both titanium surfaces, as a diode laser, light-emitting diode (LED), and laser treatment did not show any alteration on the rough and smooth titanium surfaces. Thus, a non-metallic instrument such as a plastic curette, rubber cups, and novel technology including diode laser, LED, and laser treatment is appropriate and can be used for debridement on smooth and machined titanium implant surfaces as well as sandblasted and acid-etched (SLA), titanium plasma-sprayed (TPS), and resorbable blasted media (RBM) surfaces. The use of metallic instruments should be avoided, and it is not recommended., Competing Interests: The authors have declared that no competing interests exist., (Copyright © 2022, Yen Nee et al.)