The a.c. magnetization characteristics of NdBa 2 Cu 3 O y (Nd123) bulk superconductors were investigated using a.c. susceptometry. For the present study, an OCMG-processed Nd123 bulk sample (OCMG-Nd123; T c = 93.9 K ) and a flux-grown Nd123 single crystal (Nd123SC; T c = 93.2 K ) were used. An MPMG-processed Y123 bulk sample (MPMG-Y123; T c = 91.6 K ) was also studied for comparison. While the fundamental responses are basically the same for all samples, the third harmonic responses by sweeping the bias field, x 3 ( H dc ), show an interesting feature in that the x 3 ( H dc ) curves for Nd123 samples indirectly reflect the fishtail peak of their d.c. magnetization hysteresis ( M-H ) curves. The boundary lines of Nd123 samples, determined from both the peak temperature ( T p ) of the x 1 ″( T ) maxima and the offset of the x 3 ( H dc ), are commonly located at higher field-temperature region relative to that of the Y123. Using the scaling relationship of H ∞(1 − t ) n , where t = T / T c , all the boundary lines from the x 3 ( H dc ) and the x 1 ″( T ) maxima could be best fit with a power n of ~ 1.2 and ~ 1.4, respectively.

We have measured trapped field distributions by scanning a Hall probe on various rectangular YBCO bulk superconductors and studied the effects of field dependence of Jc bulk thickness and bulk size on the trapped field. The trapped field could be increased by increasing the bulk thickness and size. However, a saturation was observed for the maximum thickness. We also calculated the distribution of trapped field taking account of the field dependence of Jc. Experimental trapped field distributions were in good agreement with our calculated values when we used the Jc-B curves obtained from a d.c. magnetization measurement for samples.