Search

The plastic waste has huge potential being used as the aggregate of concrete but the premise requires to have a sound understanding about the seepage mechanical properties of the light-weight concrete. In this study, initially, the physical experiment was conducted to measure the permeability and porosity of light-weight concrete with various amount of plastic waste aggregate (PWA) in different confining pressure and pore pressure. Based on the test results, a database was established. On this basis, a unique machine learning method was developed via combining the Logic Development Algorithm (LDA) with the ensemble technique of Adaptive Boosting Algorithm (BA) and Artificial Neural Network (ANN), which is the first attempt to utilize this model for estimating the permeability of PWA cement mortar. The research outcomes indicate, the corrected permeability and porosity of PWA cement mortar rises with the increase of PWA content, and the changing magnitude is more significant in high confining pressure; The corrected permeability and porosity of cement mortar with a higher content of PWA is more sensitive to the variation of confining pressure; The BA-ANN model optimised by LDA outperforms than the conventional machine learning models in terms of predictive accuracy and efficiency when assessing the permeability of PWA cement mortar; The sensitivity analysis by using the novel model reveals that confining pressure, PWA content and porosity have a relatively high impact on the permeability of PWA cement mortar, while the impact of pore pressure is relatively small. The study findings can provide guidance for the permeability and porosity design of relevant PWA concrete engineering facilities. • Permeability and porosity tests on plastic waste aggregate concrete were conducted. • A unique machine learning method was developed based on the experimental results. • Permeability of the concrete was preciously estimated by using the developed model. [ABSTRACT FROM AUTHOR]

• A method for preparing cement mortar with diverse numbers of internal cracks was proposed. • Permeability and porosity for the samples under diverse stress states were measured. • The stress-dependent permeability and porosity for the prepared samples was analysed. In this paper, gas permeability and porosity for the prepared cement mortar samples with diverse numbers of internal cracks under diverse pore pressure during confining pressure loading and unloading was measured. According to the outcomes of experiments, the following findings were obtained: Klinkenberg correction is appliable to the modification on gas permeability of cement mortar samples containing different number of internal cracks to obtain the intrinsic permeability, with the quadratic equation (Coefficient of Determination R2 is above than 0.92) having a better performance than that of Klinkenberg equation; Owing to the increase in the equivalent pore radius of seepage passages, Klinkenberg Effect of the cement mortar samples reduces when the number of internal cracks rises. When the number of internal cracks rises from 0 to 12, the slippage factor decreases over 90 %; When the number of internal cracks is high, the same changing extent in the number of internal cracks can lead to higher influence on the intrinsic permeability than that when the number of internal cracks is low. The variation magnitude of intrinsic permeability when the number of internal cracks increases from 6 to 12 is around 3–10 times higher than that when the number goes up from 0 to 6; When confining pressure increases, the sensitivity of intrinsic permeability to the changes in confining pressure reduces. The variation magnitude of intrinsic permeability when confining pressure is loaded from 0 MPa to 25 MPa is 5–10 times higher than that when confining pressure is loaded from 25 MPa to 45 MPa; Owing to the permanent deformation of pores and cracks, under the same confining pressure, the intrinsic permeability and porosity during the unloading stage are less than those during the loading stage, respectively; The sub-cubic law (R2 is above than0.90) is able to describe gas seepage in cement mortar specimens with different number of internal cracks more precisely compared to the cubic law. [ABSTRACT FROM AUTHOR]