A bio-flame retardant filler was synthesized via the self-polymerization of dopamine hydrochloride in alkaline condition, yielding nano-sized polydopamine (nano-PDA) particles ranging between 50 and 100 nm in diameters. Adding a small amount (2 wt%) of the nano-PDA particles into an epoxy can remarkably reduce the value of peak heat release rate by 53.6%, exceeding the performance aluminum trihydroxide (ATH) particles at 10 wt%. The significant improvement in flame retardancy at a relatively low loading of PDA has been found to originate from several key mechanisms including radical scavenging, higher char yield, and production of CO 2. Furthermore, the addition of nano-PDA in the epoxy resin increased the tensile strength by ~6%. In contrast, the addition of common flame retardant, such as ATH, to achieve the same increase in flame retardancy of epoxy would reduce the tensile strength by 22%. This improvement in mechanical properties is attributed to the better bonding between PDA particles with epoxy than ATH with epoxy. [ABSTRACT FROM AUTHOR]

The SiO 2 @metal organic framework (Universitetet i Oslo-66, UiO-66) core–shell microspheres were constructed through covalent linkage between amine groups in UiO-66-NH 2 and epoxy groups on the surface of silica. The morphology and size of the SiO 2 @UiO-66 core–shell microspheres could be simply controlled by tuning the ratio between UiO-66-NH 2 and epoxy terminated silica (E-SiO 2). As observed by TEM, the SiO 2 @UiO-66 hybrids showed better dispersion state within epoxy matrix compared to either E-SiO 2 or UiO-66-NH 2. The incorporation of SiO 2 @UiO-66 hybrids slightly promoted the thermal degradation of the resultant epoxy composites but improved residual yield. The dynamic mechanical analysis results indicated that the SiO 2 @UiO-66 hybrids slightly increased the glass transition temperature and the modulus. The SiO 2 @UiO-66 hybrids exhibited higher efficiency in reducing the heat release rate and the smoke production rate compared to either E-SiO 2 or UiO-66-NH 2. The influence of the component ratio in SiO 2 @UiO-66 on flame retardancy of the epoxy composites was also studied by cone calorimeter. Specifically, the SiO 2 @UiO-66 hybrid with medium ratio (SiO 2 @UiO-66-2) exhibited maximum reduction in peak heat release rate (−31%), total heat release (−23%) and total smoke production (−16%). The char residues were investigated by the Fourier transform infrared spectra, scanning electron microscopy and X-ray photoelectron spectroscopy, which demonstrated that the enhanced flame retardancy of EP/SiO 2 @UiO-66-2 was attributable to the continual morphology and high thermal resistance originated from the presence of the silicon and zirconium complex. These favorable characteristics including high flame retardant efficiency and good smoke suppression make SiO 2 @UiO-66 hybrids promising for flame retardant polymers application. • The SiO 2 @UiO-66 hybrids showed core–shell microsphere structure. • The addition of 3 wt% SiO 2 @UiO-66-2 caused 31% reduction in peak heat release rate. • The addition of 3 wt% SiO 2 @UiO-66-2 led to 16% reduction in total smoke production. [ABSTRACT FROM AUTHOR]