Search

Objectives: The purpose of the present prospective case series was to investigate the clinical and radiological outcome of one-piece zirconia implants fabricated from 3Y-TZP with a moderately roughened endosseous surface (Sa = 1.24 μm) to support three-unit fixed dental prostheses (FDP) after five years in function., Materials and Methods: Twenty-seven patients received a total of 54 implants in a one-stage surgery with immediate provisionalization. Peri-implant bone loss was assessed using standardized radiographs. Additionally, soft-tissue parameters were analyzed. Statistical analyses were conducted using linear mixed regression models and Wilcoxon Signed Rank tests (p < 0.05). All patients participated in an annual maintenance program., Results: Eighteen implants were lost up to the 5-year follow-up, resulting in a cumulative survival rate of 66.67%. The mean marginal bone loss of the remaining implants amounted to 1.89 mm. Probing depth, clinical attachment loss, and bleeding on probing increased from prosthesis insertion to the 5-year follow-up, while the plaque index showed no significant changes during the same period., Conclusions: The investigated one-piece zirconia implant showed low survival rates as compared to previously reported survival rates of one-piece zirconia or two-piece titanium implants. Implant failure was attributed to peri-implantitis, leading to the necessity of implant removal. The implant is not commercially available., (© 2025 The Author(s). Clinical Oral Implants Research published by John Wiley & Sons Ltd.)

Objectives: The aim of this study was to evaluate the effect of sterilization on the retention forces of lithium disilicate (LD) and polymer-infiltrated ceramic network (PICN) crowns bonded to titanium base (Ti-base) abutments., Materials and Methods: Forty LD and 40 PICN crowns were milled and then bonded to 80 Ti-bases with two resin composite cements: Multilink Hybrid Abutment (mh) and Panavia V5 (pv) for a total of 8 groups (n = 10). Half of the specimens (test) underwent an autoclaving protocol (pressure 1.1 bar, 121°C, 20.5 min) and the other half not (control). Restorations were screw-retained to implants, and retention forces (N) were measured with a pull-off testing machine. The surfaces of the Ti-bases and the crowns were inspected for the analysis of the integrity of the marginal bonding interface and failure mode. Student's t-test, chi-square test, and univariate linear regression model were performed to analyze the data (α = 0.05)., Results: The mean pull-off retention forces ranged from 487.7 ± 73.4 N to 742.2 ± 150.3 N. Sterilized groups showed statistically significant overall higher maximum retention forces (p < .05), except for one combination (LD + mh). Sterilization led to an increased presence of marginal gaps and deformities compared to no-sterilization (p < .001), while no statistically significant relationship was found between failure mode and sterilization (p > .05)., Conclusions: Sterilization may have a beneficial effect on the retention forces of LD and PICN crowns bonded to titanium base abutments, although it may negatively influence the integrity of the marginal bonding interface., (© 2024 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.)

Objective: The objectives of the study were to assess the survival, failure, and technical complication rates of implant-supported fixed dental prosthesis (iFDPs) with pontic or splinted crown (iS p C) designs in the posterior area and compare the influence of prosthetic materials and prosthetic design on the outcomes., Methods: Electronic and manual searches were performed to identify randomized-, prospective-, and retrospective clinical trials with follow-up time of ≥12 months, evaluating the clinical outcomes of posterior iFDPs with pontic or iS p Cs. Survival and complication rates were analyzed using robust Poisson's regression models., Results: Thirty-two studies reporting on 42 study arms were included in the present systematic review. The meta-analysis of the included studies indicated estimated 3-year survival rates of 98.3% (95%CI: 95.6-99.3%) for porcelain-fused-to-metal (PFM) iFDPs, 97.5% (95%CI: 95.5-98.7%) for veneered zirconia (Zr) iFDPs with pontic, 98.9% (95%CI: 96.8-99.6%) for monolithic or micro-veneered zirconia iFDPs with pontic, and 97.0% (95%CI: 84.8-99.9%) for lithium disilicate iFDPs with pontics. The survival rates for different material combination showed no statistically significant differences. Veneered restorations, overall, showed significantly (p < .01) higher ceramic fracture and chipping rates compared with monolithic restorations. Furthermore, there was no significant difference in survival rates (98.3% [95%CI: 95.6-99.3%] vs. 99.1% [95%CI: 97.6-99.7%]) and overall complication rates between PFM iFDPs with pontic and PFM iS p Cs., Conclusions: Based on the data identified by this systematic review, PFM, veneered Zr, and monolithic Zr iFDPs with pontic and iS p Cs showed similarly high short-term survival rates in the posterior area. Veneered restorations exhibit ceramic chipping more often than monolithic restorations, with the highest fracture rate reported for veneered Zr iFDPs., (© 2023 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.)

Objective: To investigate the fracture strength and potential phase transformation of an injection-molded two-piece zirconia implant restored with a zirconia abutment after loading and/or aging., Methods: Thirty-two two-piece zirconia implants (4.0 mm diameter) restored with zirconia abutments were embedded according to ISO 14801 and divided into four groups (n = 8/group): Three groups were either exclusively hydrothermally treated (group HT; 85°C), dynamically loaded (group DL; 10 7  cycles; 98 N), or subjected to both treatments simultaneously (group DL/HT). One group remained untreated (group 0). A sample from each group was cross-sectioned and examined by scanning electron microscopy for possible crystal phase transformation. The remaining samples were then loaded to fracture in a static loading test. A one-way ANOVA was used for statistical analyses., Results: During dynamic loading, three implants of group DL and six implants of group DL/HT fractured at a load of 98 N. The fracture strength of group DL/HT (108 ± 141 Ncm) was significantly reduced compared to the other groups (group 0: 342 ± 36 Ncm; HT: 363 ± 49 Ncm; DL: 264 ± 198 Ncm) (p < .05). Fractures from group 0 and HT occurred at both implant and abutment level, whereas implants from group DL and DL/HT fractured only at implant level. A shallow monoclinic transformation zone of approximately 2 μm was observed following hydrothermal treatment., Conclusions: Within the limitations of this study, it can be concluded that dynamic loading and the combination of loading and aging reduced the fracture strength of the implant abutment combination. Hydrothermal treatment caused a shallow transformation zone which had no influence on the fracture strength., (© 2022 The Authors. Clinical Oral Implants Research published by John Wiley & Sons Ltd.)

Objective: To evaluate the influence of artificial aging on the transformation propagation and fracture resistance of zirconia implants., Methods: One-piece (with integrated implant abutment, 1P; regular diameter [4.1mm]; n = 16) and two-piece (with separate implant abutment, 2P; wide diameter [5 mm]; n = 16) zirconia implants were embedded according to ISO 14801. A two-piece titanium-zirconium implant (Ti-Zr; 4.1 mm diameter) served as a control (n = 16). One subgroup (n = 8) of each system was simultaneously dynamically loaded (10 7 cycles; 98N) and hydrothermally aged (85°C, 58 days), while the other subgroup (n = 8) remained untreated. Finally, specimens were statically loaded to fracture. Potential crystal phase transformation was examined at cross sections using scanning electron microscopy (SEM). A multivariate linear regression model was applied for statistical analyses., Results: The fracture resistance of 1P (1,117 [SD = 38] N; loaded/aged: 1,009 [60] N), 2P (850 [36] N; loaded/aged: 799 [84] N), and Ti-Zr implants (1,338 [205] N; loaded/aged: 1,319 [247] N) was not affected significantly by loading/aging (p = .171). However, when comparing the systems, they revealed significant differences independent of loading/aging (p ≤ .001). Regarding the crystal structure, a transformation zone was observed in SEM images of 1P only after aging, while 2P showed a transformation zone even before aging. After hydrothermal treatment, an increase of this monoclinic layer was observed in both systems., Conclusions: The Ti-Zr control implant showed higher fracture resistance compared to both zirconia implants. Loading/aging had no significant impact on the fracture resistance of both zirconia implants. The wide-body 2P zirconia implant was weaker than the regular body 1P implant., (© 2021 The Authors. Clinical Oral Implants Research published by John Wiley & Sons Ltd.)

Objectives: Soft-tissue volume augmentation treatments do not provide the satisfactory long-term functional and esthetic outcomes. The aim of the study was to develop a standardized digital procedure to design individual soft-tissue substitutes (STS) and apply mathematical modeling to obtain average shape STS for single posterior tooth defects., Material and Methods: Thirty-three casts from 30 patients were scanned. STS were designed with a computer-aided design software and a systematic procedure standardized the measurements across all STS using 3D-analysis software. The occlusal, mesial-distal, and buccal-lingual planes were defined to partition, each STS and produce a mesh. The thickness values of each 3D slice were documented in a coordinate system chart to generate a scatter graph. Graphs were embedded into images (Orange software) and images were analyzed via hierarchical clustering., Results: Three STS groups were identified according to shape. Two shapes corresponded to the maxilla defects: a square (n = 13) with dimensions of 10 mm in a lingual-buccal (length) and 7-10 mm in a mesial-distal (width) direction; a rectangle (n = 11) of 11 mm in length and 4-7 mm in width. The average shape for mandible defects (n = 9) was smaller (6-8 mm in length, 5-10 mm in width). The highest thickness in all STS was in the buccal portion, above the alveolar ridge, with median values of 2 mm. The lowest thickness of 0.2 mm was at the edges., Conclusions: The study developed novel methodology to design customized, as well as average shape STS for volume augmentation. Future STS harboring adapted geometry might increase volume augmentation efficiency and accuracy, while reducing surgical time., (© 2021 The Authors. Clinical Oral Implants Research published by John Wiley & Sons Ltd.)

Objectives: To evaluate mechanical stability (survival and complication rates) and bending moments of different all-ceramic monolithic restorations bonded to titanium bases (hybrid abutment-crowns) or to customized titanium abutments compared to porcelain-fused-to-metal crowns (PFM) after thermo-mechanical aging., Material and Methods: Sixty conical connection implants (4.3 mm-diameter) were divided in five groups (n = 12): PFM using gold abutment (GAbut-PFM), lithium disilicate crown bonded to customized titanium abutment (TAbut+LDS), lithium disilicate abutment-crown bonded to titanium base (TiBase+LDS), zirconia abutment-crown bonded to titanium base (TiBase+ZR), polymer-infiltrated ceramic-network (PICN) abutment-crown bonded to titanium base (TiBase+PICN). Simultaneous thermocycling (5°-55°C) and chewing simulation (1,200,000-cycles, 49 N, 1.67 Hz) were applied. Catastrophic and non-catastrophic events were evaluated under light microscope, and survival and complication rates were calculated. Specimens that survived aging were loaded until failure and bending moments were calculated., Results: Survival rates after aging were 100% (TAbut+LDS, TiBase+LDS), 91.7% (GA-PFM), 66.7% (TiBase+ZR) and 58.3% (TiBase+PICN) and differed among the groups (p = .006). Non-catastrophic events as screw loosening (GA-PFM) and loss of retention or micro-/macro-movement (TiBase groups) were observed. Complication rates varied among the groups (p < .001). TiBase+PICN had lower bending moment than all the other groups (p < .001)., Conclusions: Hybrid abutment-crowns made of lithium disilicate can be an alternative to PFM-based restorations, although concerns regarding the bonded interface between the titanium base and abutment-crown can be raised. PICN and zirconia may not be recommended due to its inferior mechanical and bonding outcomes, respectively. Titanium customized abutment with bonded lithium disilicate crown appears to be the most stable combination., (© 2020 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.)