Search

Cooling [Fe(bbtr)3](BF4)2 (bbtr=1,4‐di(1,2,3‐triazol‐1‐yl)butane) triggers very slow spin crossover below 80 K (T1/2↓=76 K). The spin crossover (SCO) is accompanied by a hysteresis loop (T1/2↑=89 K). In contrast to isostructural perchlorate analogue [Fe(bbtr)3](ClO4)2 in which spin crossover during cooling is preceded by phase transition at TPT=126 K in tetrafluoroborate phase transition does not occur to the beginning of spin crossover (80 K). Studies of mixed crystals [Fe(bbtr)3](BF4)2(1‐x)(ClO4)2x (0.5≤x≤0.9) showed that a phase transition precedes spin crossover, however, for x≅0.46 intersection of T1/2(x) and TPT(x) dependencies takes place. The application of pressure of 1 GPa shifts the spin crossover in [Fe(bbtr)3](BF4)2 to a temperature above 270 K. High‐pressure studies of neat tetrafluoroborate and perchlorate, as well as mixed crystals [Fe(bbtr)3](BF4)2(1‐x)(ClO4)2x (0.1≤x≤0.9), revealed that at 295 K P1/2 value changes linearly with x indicating similar mechanism of spin crossover under elevated pressure in all systems under investigation. Variable pressure single crystal X‐ray diffraction studies confirmed that in contrast to thermally induced spin crossover undergoing differently in tetrafluoroborate and perchlorate an application of high pressure removes this differentiation leading to a similar mechanism depending at first on start spin crossover and then P‐3→P‐1 phase transition occurs. In this report we have shown that 2D coordination polymer [Fe(bbtr)3](BF4)2 (bbtr=1,4‐di(1,2,3‐triazol‐1‐yl)butane) treated to date as spin crossover silent shows thermally induced spin crossover phenomenon. Spin crossover in tetrafluoroborate is extremely slow. Determination of the spin crossover curve required carrying measurement in the settle mode‐cooling from 85 to 70 K took about 600 h (average velocity of change of temperature ca. 0.0004 K/min). [ABSTRACT FROM AUTHOR]

Cooling [Fe(bbtr)3](BF4)2 (bbtr=1,4‐di(1,2,3‐triazol‐1‐yl)butane) triggers very slow spin crossover below 80 K (T1/2↓=76 K). The spin crossover (SCO) is accompanied by a hysteresis loop (T1/2↑=89 K). In contrast to isostructural perchlorate analogue [Fe(bbtr)3](ClO4)2 in which spin crossover during cooling is preceded by phase transition at TPT=126 K in tetrafluoroborate phase transition does not occur to the beginning of spin crossover (80 K). Studies of mixed crystals [Fe(bbtr)3](BF4)2(1‐x)(ClO4)2x (0.5≤x≤0.9) showed that a phase transition precedes spin crossover, however, for x≅0.46 intersection of T1/2(x) and TPT(x) dependencies takes place. The application of pressure of 1 GPa shifts the spin crossover in [Fe(bbtr)3](BF4)2 to a temperature above 270 K. High‐pressure studies of neat tetrafluoroborate and perchlorate, as well as mixed crystals [Fe(bbtr)3](BF4)2(1‐x)(ClO4)2x (0.1≤x≤0.9), revealed that at 295 K P1/2 value changes linearly with x indicating similar mechanism of spin crossover under elevated pressure in all systems under investigation. Variable pressure single crystal X‐ray diffraction studies confirmed that in contrast to thermally induced spin crossover undergoing differently in tetrafluoroborate and perchlorate an application of high pressure removes this differentiation leading to a similar mechanism depending at first on start spin crossover and then P‐3→P‐1 phase transition occurs. In this report we have shown that 2D coordination polymer [Fe(bbtr)3](BF4)2 (bbtr=1,4‐di(1,2,3‐triazol‐1‐yl)butane) treated to date as spin crossover silent shows thermally induced spin crossover phenomenon. Spin crossover in tetrafluoroborate is extremely slow. Determination of the spin crossover curve required carrying measurement in the settle mode‐cooling from 85 to 70 K took about 600 h (average velocity of change of temperature ca. 0.0004 K/min). [ABSTRACT FROM AUTHOR]

Reaction of 1,2‐di(tetrazol‐2‐yl)ethane (ebtz) with Fe(BF4)2⋅6 H2O in different nitriles yields one‐dimensional coordination polymers [Fe(ebtz)2(RCN)2](BF4)2⋅nRCN (n=2 for R=CH3 (1) and n=0 for R=C2H5 (2) C3H7 (3), C3H5 (4), CH2Cl (5)) exhibiting spin crossover (SCO). SCO in 1 and 3–5 is complete and occurs above 160 K. In 2, it is shifted to lower temperatures and is accompanied by wide hysteresis (T1/2↓=78 K, T1/2↑=123 K) and proceeds extremely slowly. Isothermal (80 K) time‐resolved single‐crystal X‐ray diffraction studies revealed a complex nature for the HS→LS transition in 2. An initial, slow stage is associated with shrinkage of polymeric chains and with reduction of volume at 77 % (in relation to the difference between cell volumes VHS−VLS) whereas only 16 % of iron(II) ions change spin state. In the second stage, an abrupt SCO occurs, associated with breathing of the crystal lattice along the direction of the Fe–nitrile bonds, while the nitriles reorient. HS→LS switching triggered by light (808 nm) reveals the coupling of spin state and nitrile orientation. The importance of this coupling was confirmed by studies of [Fe(ebtz)2(C2H5CN/C3H7CN)2](BF4)2 mixed crystals (2 a, 2 b), showing a shift of T1/2 to higher values and narrowing of the hysteresis loop concomitant with an increase of the fraction of butyronitrile. This increase reduces the capability of nitrile molecules to reorient. Density functional theory (DFT) studies of models of 1–5 suggest a particular possibility of 2 to adopt a low (140–145°) value of its Fe‐N‐C(propionitrile) angle. [ABSTRACT FROM AUTHOR]

The abrupt high spin (HS)→low spin (LS) transition (T↓1/2=136 K) in [Fe(hbtz)2(CH3CN)2](BF4)2 (hbtz=1,6‐di(tetrazol‐2‐yl)hexane) is finished at 100 K and further thermal treatment influences the spin crossover. Subsequent heating involves a change of the spin state in the same way (T↑1/2=136 K) on cooling. In contrast, cooling below 100 K triggers different behavior and T↑1/2 is shifted to 170 K. The extraordinary structural changes that occurred below 100 K are responsible for the observed diversity of properties. A unique feature of the low‐temperature phase is the rebuilding of the anion network expressed by a shift of anions inside the polymeric layer at a distance of 1.2 Å as well as the relative shift of neighboring layers at over 4 Å. These structural alterations, connected with a phase transition, become the origin of the strain, which in most cases causes crystal cleaving. In a sample composed from crystals crushed as a result of the phase transition or as a result of mechanical crumbling, the hysteresis loop vanishes; however, annealing the sample allows to its partial restoration. A replacement of acetonitrile by other nitriles leads to preservation of the polymeric structure and spin crossover, but no phase transition follows. Spin and phase transitions: Two‐dimensional coordination network [Fe(hbtz)2(CH3CN)3](BF4)2 (hbtz=1,6‐di(tetrazol‐2‐yl)hexane) exhibits a high spin (HS)⇄low spin (LS) transition, which is accompanied by significant structural changes, in particular, involving the shift of neighboring polymeric layers at distances above 4 Å. Occurrence of a structural phase transition as well as hysteresis loop is blocked by crystal cleavage, however, sample annealing restores hysteretic behavior (see scheme). [ABSTRACT FROM AUTHOR]

The abrupt high spin (HS)→low spin (LS) transition (T↓1/2=136 K) in [Fe(hbtz)2(CH3CN)2](BF4)2 (hbtz=1,6‐di(tetrazol‐2‐yl)hexane) is finished at 100 K and further thermal treatment influences the spin crossover. Subsequent heating involves a change of the spin state in the same way (T↑1/2=136 K) on cooling. In contrast, cooling below 100 K triggers different behavior and T↑1/2 is shifted to 170 K. The extraordinary structural changes that occurred below 100 K are responsible for the observed diversity of properties. A unique feature of the low‐temperature phase is the rebuilding of the anion network expressed by a shift of anions inside the polymeric layer at a distance of 1.2 Å as well as the relative shift of neighboring layers at over 4 Å. These structural alterations, connected with a phase transition, become the origin of the strain, which in most cases causes crystal cleaving. In a sample composed from crystals crushed as a result of the phase transition or as a result of mechanical crumbling, the hysteresis loop vanishes; however, annealing the sample allows to its partial restoration. A replacement of acetonitrile by other nitriles leads to preservation of the polymeric structure and spin crossover, but no phase transition follows. Spin and phase transitions: Two‐dimensional coordination network [Fe(hbtz)2(CH3CN)3](BF4)2 (hbtz=1,6‐di(tetrazol‐2‐yl)hexane) exhibits a high spin (HS)⇄low spin (LS) transition, which is accompanied by significant structural changes, in particular, involving the shift of neighboring polymeric layers at distances above 4 Å. Occurrence of a structural phase transition as well as hysteresis loop is blocked by crystal cleavage, however, sample annealing restores hysteretic behavior (see scheme). [ABSTRACT FROM AUTHOR]