A simple one-pot synthesis of size and shape controlled ZnTe nanocrystals using a monomeric molecular precursor, [Zn(TePh)2][TMEDA], has been studied by varying the growth temperature or the templating surfactants.

One-step size-controlled synthesis of ZnSe quantum dots is studied and the obtained QDs are luminescent with the emission wavelength varying over a wide range (up to 100 nm) depending on the particle size; the single-molecular precursor is an air-stable bis(phenylselenolato)zinc N,N,N′,N′-tetramethylethylenediamine (TMEDA) complex, which effectively affords different sizes of ZnSe QDs depending on growth temperatures.

A magnetic field is successfully utilized to induce the fabrication of size controllable one-dimensional (1-D) supercrystals which are composed of a highly crystalline assembly of fcc-packed cobalt nanoparticles; the anisotropy associated supercrystal magnetism is enhanced with four times higher coercivity than that of randomly aggregated nanoparticles.

Remarkable selectivity is achieved in the cleavage of benzyl ethers using ball-shaped palladium nanocatalysts, Pd@MCM-48, in an MCM-48 matrix. The unique nanocatalysts not only feature unprecedented complete hydrogenolysis selectivity of a benzyl ether over hydrogenation of a double bond, but also demonstrate selective cleavage of unsubstituted benzyl ether over substituted benzyl ethers.

A simple procedure for the fabrication of sub-10 nm scale Si nanopillars in a 2-D array using reactive ion etching with 8 nm Co nanoparticles as etch masks is demonstrated. The obtained Si nanopillars are single crystalline tapered pillar structures of 5 nm (top) x 8 nm (bottom) with a density of approximately 4 x 10(10) pillars cm(-2) on the substrate, similar to the density of Co nanoparticles distributed before the ion etching process. The uniform spatial distribution of the Si nanopillars can also be patterned into desired positions. Our fabrication method is straightforward and requires mild process conditions, which can be extended to patterned 2-D arrays of various Si nanostructures.