Search

Metal‐organic frameworks (MOFs) have been considered as promising platforms for preparing the efficient oxygen evolution reaction (OER) catalysts, but few of them are directly employed as active components due to their poor electrical conductivity. Herein, a lamellar bimetallic MFN (MIL‐53(FeNi)) encapsulated in graphene aerogel‐grafted Ni foam has been developed (denoted as MFN@GA/NF). The graphene aerogel (GA) provides abundant space for the in‐situ growth of MFN and functions as a "bridge" to connect nickel foam (NF) with MFN by virtue of good conductivity. Benefitting from its structural integrity, the obtained hierarchical MFN@GA/NF exhibited excellent OER performances in alkaline media with an overpotential of 250 mV (20 mA cm−2) and 326 mV (200 mA cm−2), as well as remarkable stability in continuous electrolysis for over 100 h. This work provides a new channel for engineering MOF‐based functional materials with featured architectures. [ABSTRACT FROM AUTHOR]

The fabrication of cost‐effective and performance‐advanced electrocatalysts is in great requirements for water splitting to achieve sustainable oxygen production. A simple and effective precursor of ZIF‐67 particles mounted on Cu(OH)2 nanorods was induced by a template alignment method. After annealing, hierarchical CoO polyhedron‐decorated CuO/Cu2O (CuOx) nanorods on Cu foam (denoted as CuOx@CoO NRs/CF) were achieved, which displayed the heterojunction in CuOx components, hierarchical configuration and outward active sites. These features, verified by HRTEM, SEM, XPS and EDX, optimized the oxygen evolution reaction (OER) electrocatalyst. Benefiting from its large electrochemical surface area and the synergetic effect between CuOx and CoO, CuOx@CoO NRs/CF exhibited considerable catalytic activity with a low overpotential of 254 mV to obtain a current density of 10 mA cm−2 in alkaline electrolyte and a scarce loss of the initial catalyst activity over 24 h and over 5000 cycles. This work provides a channel to enhance the performance in OER. [ABSTRACT FROM AUTHOR]

The fabrication of non‐noble element electrocatalysts with comparable catalytic activity with Pt‐based materials is in great requirements for water splitting to achieve sustainable hydrogen production. Cu2S/MoS2 heterojunction nanorod arrays on copper foam were prepared for this purpose. The nitrogen doping was achieved in situ. HRTEM, SEM, XPS and EDX verified the heterojunction interfacial texture and the defect‐rich nanoarray configuration. The heterojunction interfacial texture, the defect rich configuration and the outward active sites optimized the structure required as a high‐efficient hydrogen evolution reaction (HER) electrocatalyst. As a result, the charge transfer resistance of the nanoarrays was estimated to be 5.4 Ω at −200 mV versus RHE, even lower than both the precursors. The electrochemical double layer capacitance was 49.95 mF cm−2, which was higher than both the precursors. The Cu2S/MoS2 heterojunction nanoarrays‐like electrocatalyst exhibited significant performance with a low overpotential (91 mV at 10 mA cm−2) and a small Tafel slope (41 mV dec−1) in alkaline electrolyte with 85.3 % retained ability after 1000 cycle runs. This work paves a road for developing high‐performance HER electrocatalysts. His and HER: Nitrogen doped Cu2S/MoS2 heterojunction nanorod arrays grafted on copper foam in situ have been created for efficient hydrogen evolution reaction. The results showed the remarkably improved catalytic activity by designing and tuning the heterostructure, conductivity and active sites. [ABSTRACT FROM AUTHOR]