Search

Paper with simultaneous fire-resistance and hydrophobicity have greatly potential applications in the fields of packing, storage and delivering information, which attracts increasing attention recently. Different from the traditional cellulose-based paper which is extremely easily damaged by water and fire, a new type of highly flexible, fire-resistant and hydrophobic paper based on Si 3 N 4 nanowires and polydimethylsiloxane (PDMS) is reported. Specially, the Si 3 N 4 @PDMS core-shell nanowires with 3D interlocking structure are designed, in which the Si 3 N 4 nanowires act as the inorganic fire-resistant frameworks and the PDMS shell with low surface energy provides the hydrophobic surface. The Si 3 N 4 @PDMS core-shell nanowires are intertwined and interlaced to form a highly flexible Si 3 N 4 @PDMS paper. The tensile strength of Si 3 N 4 @PDMS paper is 6.19 MPa, indicating the good mechanical property. The obtained Si 3 N 4 @PDMS paper has the characteristics of writability, fire-resistance and hydrophobicity. The high thermal stability of Si 3 N 4 nanowires makes Si 3 N 4 @PDMS paper exhibit excellent fire resistance. No obvious change is observed for the commercial paper with Si 3 N 4 @PDMS paper as the fire-shielding layer after heating for 30 min. In addition, the contact angles of water droplets are all greater than 110° over the surfaces of Si 3 N 4 @PDMS paper after mechanical damages, chemical corrosions and thermal treatments. Si 3 N 4 @PDMS paper can be used in oil/water separation and oil collection. More importantly, Si 3 N 4 @PDMS paper can be used for writing without being damaged by fire or water. The present work may inspire the development and application of functional paper and is expected to become a breakthrough in the traditional paper industry. [ABSTRACT FROM AUTHOR]

The development of self-powered UV photodiode on green substrate is still a challenge. In this study, highly conductive Al doped ZnO (AZO) film was sputter-deposited on paper substrate at room temperature; subsequently, paper-based Schottky photodiodes were successfully fabricated by following Au-ZnO-Al and Au-ZnO-AZO-Al structure designs, respectively. These UV light-based devices operate successfully without external power. Au-ZnO-AZO-Al photodiode shows improved response and faster speed compared to Au-ZnO-Al photodiode. The one-dimensional Poisson simulation results demonstrate that the improvement is attributed to the strong electric field in the ZnO-AZO n-n+ high-low junction, thus, enhancing the collection rate and drifting speed of the photogenerated carriers. In addition, AZO can form favorable ohmic contact with the Al electrodes, further improving the device performance. The photo-response of the paper-based photodiode device shows high reproducibility and stability. Based on these outstanding results, we conclude that these paper-based electronic devices have great potential to replace conventional petroleum-based flexible electronic devices, thus, contributing to the green/sustainable development. [ABSTRACT FROM AUTHOR]

The synthesis of few-layer graphene from graphite typically uses N, N methyl pyrrolidone (NMP) or dimethylformamide (DMF) due to the strong affinity of both solvents for graphite. However, NMP and DMF are known as carcinogens and a long-time exposure to these substances may subject users to potential risk of major health issue later. Therefore, a replacement with dispersing solvent that is not only harmless but also able to exfoliate graphite at an excellent concentration yield must be outlined for a sustainable mass-production of graphene. In this work, we have successfully exfoliated graphite to few-layer graphene with a recorded yield concentration of up to 0.75°mg/ml (2.5°h) just by using extracted red spinach/water mixture as an exfoliating medium. The prepared graphene was found to possess less structural defect (I D /I G : 0.5) and high C/O ratio (6.8) and can be used further as an electrical conductive ink for smart "Sticky Note" sensor. The fabricated device was able to detect strain and temperature with gauge factor and temperature coefficient resistance of 23.5 and −32.14 × 10-4°Ω/°;C, respectively. We believe that this study would be useful for the preparation of environmental-friendly graphene that is not only strain and thermally sensitive but also producible at low -cost. Image 1 [ABSTRACT FROM AUTHOR]

Abstract: The purpose of this study was to increase the thermal resistance of a cellulose substrate, using films (a mixture of corundum-phase aluminum oxide, α-Al2O3, and a PVA solution). The corundum phase, which was chosen due to its high thermal resistance, was obtained using an adaptation of Pechini‘s polymeric precursor method. A polyvinyl alcohol (PVA) solution was used as a medium for mixing the oxide for subsequent deposition on a paper substrate. The materials were characterized by X-ray diffraction (XRD) and field emission gun scanning electron microscopy (FEG-SEM) coupled with energy dispersive X-ray spectrometry (EDS). The thermal behavior of the material was investigated by thermogravimetry (TG) and differential scanning calorimetry (DSC). The EDS results indicate that all the samples with deposited α-phase aluminum oxide contain the chemical elements (Al and O) originating from the α-phase, while the surface analysis indicated that the paper substrates were completely coated with the films. The TG and DSC analyses of the thermal resistance of the film-coated substrate indicate that it was impossible to increase the thermal resistance of the paper substrate because the events that occurred (decomposition of cellulose and pyrolysis of lignin, hemicellulose and PVA) took place in the same temperature range, as has been reported in the literature for samples of the paper substrate without deposited film. [Copyright &y& Elsevier]

The effect of calendering of alumina loaded preceramic papers in a hard nip laboratory calender at various temperatures, line loads and times of nip passes on their green and sintered properties was investigated. The main objective was to achieve a maximum densification, which resulted in a maximum reduction of thickness of 45%, a green density of 80.5% of the theoretical density and a sintered density of 81% of the theoretical density. The ring-on-ring flexural strength of sintered specimen could be increased from 71±11MPa to 138±33MPa. The surface roughness of green samples could be diminished to a value for R a of below 2µm compared to an R a of 13.2µm for an uncalendered paper, whereas the R a value of the sintered samples was much higher due to the burn-off of the cellulose fibers. Preceramic papers manufactured by the dynamic hand-sheet-forming process exhibit a fiber-orientation which causes anisotropic effects regarding the sintering shrinkage, the surface roughness and Young's modulus. [ABSTRACT FROM AUTHOR]