Search

High-hardness TaN compacts with a diameter and height of 6 mm were synthesized through the phase transformation of CoSn-type into WC-type TaN under experimental conditions of high temperature and high pressure. The Vickers hardness of WC-type TaN compacts obtained at the pressure of 5 GPa and the temperature of 1873 K is found to be ~21.5 ± 1.5 GPa with a load of 3 Kg, which is comparable to that of the pure tungsten carbide compact (~20 GPa) and higher than those of ultrahigh temperature ceramics ZrB 2 and HfB 2 under the same load. The high hardness of WC-type TaN compacts presented in this work is attributed to the deviatoric strain and well-bonded nanograins. The synthesized WC-type TaN compacts also possess a high oxidation temperature (1072 K). These results suggest that the WC-type TaN with high hardness and high thermal stability holds great promise for industrial applications. [ABSTRACT FROM AUTHOR]

We report a method for strengthening microcrystalline alumina compaction by work hardening under conditions of high pressure and temperature, in which the hardness significantly improved. Micro-sized spherical alumina powders were treated without additives under 5.5 GPa–14 GPa and 600 °C–1200 °C. A polycrystalline sample sintered at 12 GPa and 900 °C yielded a Vickers hardness of 30.0 GPa, which was 1.5 times that of single-crystal alumina and the highest value reported to date for alumina. By analysing the density, hardness, and microstructure of the sintered samples, the results demonstrated that under ultra-high pressure and below the recrystallisation temperature of alumina, plastic deformation of the grains produced many substructures such as stacking faults and lattice distortions showing obvious work hardening effects. Combined with well-bonded crystalline and amorphous grain boundaries, the hardness of the samples was unexpectedly enhanced. [ABSTRACT FROM AUTHOR]

Cubic boron nitride (cBN), a typical superhard material, has garnered significant interest for both fundamental scientific research and technical applications. Here, nanostructured cBN with high-density nanotwins and stacking faults was synthesized by rapid quenching using hexagonal boron nitride (hBN) as the starting material at a moderate temperature (2200 K) and low pressure (13 GPa). This synthetic nanostructured cBN exhibits high Vickers hardness (78 GPa), high fracture toughness (11.8 MPa·m1/2), and extremely high oxidization temperature (1565 K). We propose that the refined grain structure and excellent mechanical properties of the cBN synthesized in this study is attributed mainly to dislocation slips and (111) mechanical nanotwins that dominate this phase transformation. [ABSTRACT FROM AUTHOR]

High-performance polycrystalline cubic boron nitride (PcBN) was sintered without binders at 1500 °C in a pressure range from 11 to 15 GPa using commercial micrometre cubic boron nitride (cBN) with a diameter of approximately 2–4 μm. The results demonstrated that the sample sintered at 12 GPa and 1500 °C had the best mechanical properties and thermal stability. Its average Vickers hardness, fracture toughness, and thermal stability was 63 GPa, 15 MPa m1/2, and 1315 °C, respectively. The considerable improvement in the mechanical properties was mostly attributed to the high compactness, close bonding between grains, and the sample's internal defect structures. The relatively small specific surface area of the micron grains provides an advantage due to its high thermal stability. The amorphous regions observed in the sample's local areas may provide a new strengthening mechanism under high pressure and temperature. [ABSTRACT FROM AUTHOR]