Abstract: In this study, we used oxides (Y2O3, CeO2 and Al2O3) as the raw materials to fabricate YAG:Ce3+ phosphors by a molten salt synthesis (MSS) method. The formation of YAG phase strongly depends on the alumina source and firing temperature. Microstructure characterization indicates that “dissolution-precipitation” mechanism dominates the formation process of YAG in the alkali chlorides melt. Thus, highly active nano-Al2O3 starting powders promote their solution in the melt and guarantee a solute stoichiometric of YAG phase rather than other Y–Al–O compounds. The as-prepared YAG:Ce3+ phosphors show typical yellow emission peaked at 535nm under excitation of 460nm blue light, suggesting that MSS could be a promising method for the preparation of phosphor powders even though oxide raw materials are used. [Copyright &y& Elsevier]

Abstract: Tunable white light of Eu2+ doped SiAlON crystal/glass composite phosphor with blue-yellow dual-emissions was demonstrated by variation of excitation wavelength in this work. The excitation properties of blue emission originated from the transition of Eu2+ ions in the Si–Al–B–O–N glass matrix and that of yellow emission originated from the transition of Eu2+ ions in the SiAlON lattice were investigated, respectively. By varying the excitation wavelength in the range of 330–380nm, white emission was tuned from cool white to warm white for this SiAlON crystal/glass composite phosphor owing to the various excitation properties of these two emission bands. Presented results indicate that this tunable SiAlON crystal/glass composite white-light phosphor might be applied in white LED, combining with UV chips with different emitting wavelengths in the range of 330–380nm. [Copyright &y& Elsevier]