Search

Engineering highly porous SiC foams with interconnected cellular architecture and satisfactory compressive strength for the practical applications remains a challenging task. In the current work, SiC foams bonded by in-situ formed mullite phase were fabricated via polyurethane foaming using boehmite sol-coated SiC powder as the raw material. The strategy in the current work endowed the resultant products with ultrahigh porosity, interconnected pore structure, and a robust mullite bonding phase among the SiC particles. The resulting products with this cellular architecture possessed a high porosity level of 88.5% and maintained a robust compressive strength of 2.56 MPa. Our results showed that as-prepared products are promising for practical applications in the filtration, adsorption and catalytic areas. [ABSTRACT FROM AUTHOR]

Engineering high performance cellular ceramics with both ultralow density and satisfactory compressive strength for practical applications still represents a grand challenge. Herein, alumina-based cellular ceramics bonded by in-situ formed mullite phase were constructed by Al 2 O 3 –Si-boehmite particle-stabilized foams. The gelation of boehmite sol improved the stability and harnessed the deformation of dried Al 2 O 3 –Si composite foam. The oxidation of silicon and further generation of in-situ mullite phase enhanced the chemical bond between alumina particles on cell walls, resulting in the superior mechanical properties. As an exemplar, the resulting cellular ceramic possessed the robust compressive strength of 2.26 MPa at a high porosity of 87.8%. The gelation-assisted Al 2 O 3 –Si particle-stabilized foams provide a facile and convenient strategy for construction of composite ceramic foams with high porosity and robust strength. [ABSTRACT FROM AUTHOR]

Ultralight ceramics with striking mechanical properties and improved pore connectivity could have wide applications in areas ranging from catalyst support to hot gas filtration. However, creating such materials has proven to be a challenging target. This work demonstrated a novel methodology to prepare porous MgAl 2 O 4 ceramics by calcining gelled MgO–Al 2 O 3 –SiO 2 particle-stabilized foams. The striking green strength of dried foams can be achieved as a consequence of MgO hydration and subsequent formation of gelled Mg(OH) 2 and MgO–SiO 2 –H 2 O skeleton. The decomposition of colloidal substance at elevated temperature resulted in the formation of small pores on the cell wall, thus forming the hierarchical porous architecture and improving the pore connectivity. The highly porous MgAl 2 O 4 ceramics fired at 1600°C possessed the integrated properties of ultrahigh porosity (87.0%), improved pore connectivity and satisfactory compressive strength (7.93 MPa), showing great potential to be used in multiple industrial fields. [ABSTRACT FROM AUTHOR]

Compressive strength is one of the most important mechanical properties for ceramic foams but the dependence of compressive strength of highly porous ceramic foams on porosity remains unclear up to now, especially for the ceramic foams with porosity above 94%. In this paper, the relationship between compressive strength and porosity of ceramic foams with high porosity in the range of 79–98% was studied for the first time. The alumina ceramic foams and zirconia foams were prepared by particle-stabilized foaming method using sodium dodecyl sulfonate (SDS) as foaming agent. It was found that the function relation between compressive strength and porosity depended on porosity level. Specifically, compressive strength of ceramic foams fitted well with Rice Model when the porosity ranged from 79% to 94%. When the porosity increased above 95%, compressive strength of ceramic foams showed linear relation to porosity, which was probably due to the characteristic of highly porous ceramic foams with thin and lamellate cell wall. [ABSTRACT FROM AUTHOR]