Search

Graphite-based metal transition-layer substrates hold great potential for preparing large-area diamond films and achieving crack-free release. In this study, a five-inch crack-free free-standing diamond film was prepared on a graphite substrate with a sacrificial Mo/Ti double-layer transition layer using direct-current arc plasma jet chemical vapor deposition (DC jet CVD). The interfacial bonding and diffusion behavior between the diamond and the transition layers were investigated. The effect of abundant metal particles and elemental diffusion between layers on film adhesion and stress release are discussed and analyzed. The surface of Ti layer prepared by the multi-arc ion-plating contains numerous metal particles that provide a template for the fine-crystalline Mo layer. Metal particles are encapsulated and embedded in the diamond and act as anchors that ensure the stability of the substrate–diamond bond during high-temperature deposition. After deposition, those metal particles act as weak points and play crucial stress-release roles. Mutual elemental diffusion occurs between the Ti, Mo, and diamond layers. Ti penetrates the Mo layer to form a continuous 140-nm-thick thin layer during the initial deposition period, facilitating diamond nucleation. Carbon from the plasma and diamond diffuses into the metal transition layer. Thermal stress generated between the diamond and the graphite substrate is released by destroying the metal transition layer with high thermal expansion coefficient and low elastic modulus during cooling from the deposition temperature. Cracks rapidly propagate along the interface between destroyable transition layers and graphite substrate, which results in the liftoff of a fully crack-free diamond film. [Display omitted] [ABSTRACT FROM AUTHOR]

Oxygen evolution reaction (OER) is critical in water splitting for green hydrogen gas production due to its sluggish kinetics; however, commercial OER catalysts commonly suffer from high cost, low catalytic activity and poor stability. Herein, we developed a C+ ion implantation method to modify single crystal diamond, and the resultant surface amorphous layer not only raised the active site number but also increased the content of the C=O group, thus significantly improving the OER activity. The C+ ion implanted high-temperature and high-pressure (C+-HTHP) and chemical vapor deposition (C+-CVD) diamonds both exhibit low OER overpotential with η 10 of 317 mV and 325 mV respectively, superior to those of HTHP diamond (360 mV), CVD diamond (395 mV) and RuO 2 (364 mV). The potentiostatic testing shows that the C+ implanted diamonds almost didn't undergo the rise of OER overpotential upon catalysis for more than 12 h at a current density of 10 mA cm−2, suggesting a high catalytic stability, owing to the strong bonding between single crystal diamond and amorphous carbon layer. For the first time, we utilized carbon ion implantation to prepare diamond-based high-performance OER catalyst, which broadens the understanding of carbon-based materials in OER catalysis. [ABSTRACT FROM AUTHOR]

Reducing the self-heating of SiC- and GaN/SiC-based high-powered devices by integrating diamond films offers promising performance enhancement of these devices. However, such a reduction strategy faces serious problems, such as diamond nucleation on SiC and stress accumulation greater than 10 GPa. In this work, a SiN x dielectric layer (∼50 nm) was coated onto the C polar face of a 4H–SiC wafer using microwave plasma chemical vapor deposition (MPCVD) to improve direct dense diamond nucleation and growth, significantly reduce the stress, and build Si–C(SiC)⋯Si⋯C(diamond) bond bridges. This SiN x thin layer, prepared by activating Si ions under Ar/N plasma during magnetron sputtering, gave rise to local Si 3 N 4 crystal features and a low effective work function (EWF) for promoting surface dipoles with electronegative carbon-containing groups. In the H plasma environment during diamond growth, the local Si 3 N 4 crystal was amorphized, and the N atoms escaped as a result of atomic H and the high temperature. At the same time, C atoms diffused into the SiN x and formed C–Si bonds (49.7% of the total C bonds) by replacing N–Si and Si–Si, thus increasing the direct nucleation density of the diamond grains. The diamond thin film grew rapidly and uniformly, with a grain size of approximately 2 μm in mixed orientation, and the stress of the 2-inch SiC-on-diamond wafer was extremely low (to ∼0.1–0.2 GPa). In comparison, partially connected diamond grains (>10 μm) on the bare SiC in the preferential (110) orientation resulted in a film with twin-grain features and significant stress, which was associated with the hexagonal lattice interface of 4H–SiC. These results are considered the material and surface/interface bases for actively controlling wafer fabrication and enhancing the heat dissipation of SiC and GaN/SiC electronics. [ABSTRACT FROM AUTHOR]