Search

Silicon oxycarbide (SiOC) ceramics have been used to fabricate microwave-absorbing metastructures, demonstrating impressive absorption capabilities. However, SiOC ceramic metastructures with excellent performance require simple fabrication processes and appropriate mechanical and electromagnetic properties. In this study, a solvent-free photosensitive polysiloxane preceramic was developed by blending methoxy/hydroxy polysiloxanes with acrylates, with a ceramic yield of over 60% after curing using a novel two-step ultraviolet (UV)/thermal method. The composition and microstructure of SiOC ceramics can be designed by controlling the preceramic composition. Dense, crack-free gyroid-shellular shaped triple periodic minimal surface (GS-TPMS) electromagnetic metastructures were fabricated using digital light processing (DLP) 3D printing technology. By designing the porosity of the GS-TPMS structure to 51%, an effective absorption bandwidth that covers the X-band can be achieved at a thickness of 3.1 mm. The honeycomb structure, with a geometric density of 0.69 g/cm3, exhibited a high compressive strength of 107.05 MPa. This paper presents an efficient approach for the prompt and customized fabrication of lightweight ceramic metastructures with outstanding microwave absorption properties. • A solvent-free polysiloxane/acrylate hybrid preceramics is developed for 3D printing. • The UV/thermal two-stage treatment achieved cross-linking curing of the preceramics. • Multiscale design of SiOC ceramics for enhanced microwave absorption properties. • SiOC ceramic metastructures with effective absorption in the X-band are prepared. [ABSTRACT FROM AUTHOR]

In this study, Al 2 O 3 honeycomb sandwich structures with different core geometries (square, triangular, circular) have been fabricated through an additive manufacturing system based on the stereolithography (SLA) method. The debinding procedure was performed under both nitrogen and air atmospheres. The impacts of the debinding atmosphere and core geometry on the densification and mechanical properties were investigated. The stiffness and flexural strength of the ceramics were examined experimentally using an impulse excitation of vibration technique and a three-point bending test, respectively. The specific stiffness and specific strength of the ceramics were also evaluated, with the core geometries taken into consideration. The outcomes showed that higher densification was achieved when the ceramics were exposed to debinding in nitrogen. The stiffness values were found to be similar for the same debinding condition within the honeycomb sandwich structures, irrespective of the core geometry. Notably, the highest specific stiffness (98 MNm/kg) was achieved for the samples subjected to debinding in nitrogen with a square core geometry. Furthermore, ceramics with square cores for debinding in a nitrogen atmosphere also demonstrated the highest performance in terms of specific strength (110 kNm/kg) within the honeycomb structures. This study demonstrated that Al 2 O 3 honeycomb sandwich structures with square cores may be suitable candidates for lightweight-structure demanding applications. [ABSTRACT FROM AUTHOR]

Inspired by the double-helix structure of biological DNA, low-volume fraction and high-strength Al 2 O 3 twisted honeycomb structures with characteristics similar to those of helical structures in the z -axis were prepared by digital light processing 3D printing technology. As the twist angle increased, the compressive strength of the fabricated Al 2 O 3 structure decreased, and the deformation mechanism of the Al 2 O 3 structures gradually changed from stretching-dominated to bending-dominated, which can be predicted by the Gibson–Ashby model. The relationship between the effective elastic modulus and the volume fraction that can be modified by varying the wall thickness was described by the Pabst–Gregorova exponential relationship. The compressive strength of the Al 2 O 3 structure with a twist angle of 0° can reach 62.4 MPa at a volume fraction of 13.3%, providing guidance to optimize lightweight structures of ceramics. [ABSTRACT FROM AUTHOR]

Three-dimensional (3D) printing of ceramics has attracted increasing attention in various fields. However, the pyrolysis of organic components used for binding or polymerization in 3D printing commonly causes a large shrinkage (up to 30 %–40 %), high porosity, and cracking or deformation, severely limiting practical applications. In this study, 3D printing of Al 2 O 3 ceramic architectures with ultra-low shrinkage is realized by introducing inorganic binder aluminum dihydrogen phosphate (Al(H 2 PO 4) 3 , AP) as a ceramic precursor. Compared to organic binders, the inorganic AP binder can undergo crystallization conversion, which reduces mass loss during sintering at high temperatures, resulting in low shrinkage. Moreover, AP can be used as a rheological modifier to regulate the printability of the ceramic ink for direct ink writing of Al 2 O 3 ceramic architectures, such as wood-piled scaffolds, honeycomb structures, and tubes with high fidelity. The resultant Al 2 O 3 structural ceramics sintered at 1250 °C exhibit good mechanical performance and structural integrity. Most importantly, the linear shrinkage of the printed ceramics is less than 5 %, which is several times lower than that of ceramics with organic binders. This study provides a viable strategy for fabricating high-performance ceramic architectures with good dimensional fidelity for practical applications. ∙ Al 2 O 3 ceramics with aluminum phosphate binder were printed by using direct ink writing. ∙The resultant Al 2 O 3 ceramic exhibited ultra-low dimensional shrinkage owing to the inorganic binder. ∙Al 2 O 3 ceramics are programmable in size and shape, with good stability, reusability, and fidelity. [ABSTRACT FROM AUTHOR]