Engineering highly porous SiC foams with interconnected cellular architecture and satisfactory compressive strength for the practical applications remains a challenging task. In the current work, SiC foams bonded by in-situ formed mullite phase were fabricated via polyurethane foaming using boehmite sol-coated SiC powder as the raw material. The strategy in the current work endowed the resultant products with ultrahigh porosity, interconnected pore structure, and a robust mullite bonding phase among the SiC particles. The resulting products with this cellular architecture possessed a high porosity level of 88.5% and maintained a robust compressive strength of 2.56 MPa. Our results showed that as-prepared products are promising for practical applications in the filtration, adsorption and catalytic areas. [ABSTRACT FROM AUTHOR]

Engineering high performance cellular ceramics with both ultralow density and satisfactory compressive strength for practical applications still represents a grand challenge. Herein, alumina-based cellular ceramics bonded by in-situ formed mullite phase were constructed by Al 2 O 3 –Si-boehmite particle-stabilized foams. The gelation of boehmite sol improved the stability and harnessed the deformation of dried Al 2 O 3 –Si composite foam. The oxidation of silicon and further generation of in-situ mullite phase enhanced the chemical bond between alumina particles on cell walls, resulting in the superior mechanical properties. As an exemplar, the resulting cellular ceramic possessed the robust compressive strength of 2.26 MPa at a high porosity of 87.8%. The gelation-assisted Al 2 O 3 –Si particle-stabilized foams provide a facile and convenient strategy for construction of composite ceramic foams with high porosity and robust strength. [ABSTRACT FROM AUTHOR]

A facile strategy for the fabrication of elongated mullite reinforced porous alumina ceramics (PACs) using carbonized rice husk (CRH) as pore-forming agent and silica source is reported for the first time. A large amount of elongated mullite is synthesized in pores due to the reaction of amorphous silica in CRH skeleton and alumina ceramic powder. Elongated mullite acts as the bridges between pore walls, enhancing the compressive strength of PACs. Furthermore, secondary pores from the intersection of elongated mullite is favor of decreasing of the thermal conductivity. High performance PAC with porosity of 74.3% has been fabricated by employing 25 wt% CRH, which possesses relatively low thermal conductivity of 0.189 W/(m•K) and ultra-high compressive strength of 45 MPa. Its comprehensive performance is much better than that of existing ceramic materials. Our findings present a facile, eco-friendly and effective approach to fabricate high performance PACs as the high-temperature thermal insulation materials. [ABSTRACT FROM AUTHOR]