Search

Cubic ZrV 2 O 7 thin films have been synthesized by sol-gel spin-coating method. The influences of annealing temperatures on the phase composition and morphology of ZrV 2 O 7 thin films were investigated using XRD, SEM, and EDX. Negative thermal expansion (NTE) and optical performances of cubic ZrV 2 O 7 thin films were analyzed using variable temperature XRD and UV–Vis spectroscopy. Results indicate that as-deposited ZrV 2 O 7 thin films have an amorphous structure with smooth and dense surface. Cubic ZrV 2 O 7 thin films were prepared after heat treatment at 720 °C for 1 h. It was found that the thin films contained V 2 O 5 impurity with the Zr: V = 1:2 precursor solution. Pure cubic ZrV 2 O 7 thin films were fabricated with the Zr: V = 1.75:2 precursor solution. Cubic ZrV 2 O 7 thin films show isotropic NTE in the temperature range of 100–700 °C. The coefficients of thermal expansion (CTEs) of ZrV 2 O 7 films along the a , b , and c axes are −6.88 × 10−6 °C−1, and the volumetric and linear CTEs are −20.56 × 10−6 °C−1 and -6.85 × 10−6 °C−1, respectively. The transmittance of cubic ZrV 2 O 7 thin film is approximately 80 %. [ABSTRACT FROM AUTHOR]

Orthorhombic In 0.5 Sc 1.5 Mo 3 O 12 thin films have been synthesized using the sol-gel spin coating. Influences of post-annealing temperatures on crystal structure, morphology, negative thermal expansion (NTE) and optical performances of the thin films were studied using XRD, SEM, XPS, high-temperature XRD and UV–Vis–NIR spectrophotometer. XRD and SEM results show that as-prepared thin film is in an amorphous state with a smooth and dense surface. Orthorhombic In 0.5 Sc 1.5 Mo 3 O 12 thin films were obtained after post-annealing in 550–750 °C. The higher the annealing temperature in 550–750 °C, the better the crystallinity of orthorhombic In 0.5 Sc 1.5 Mo 3 O 12 thin films. In addition, the grain size of the In 0.5 Sc 1.5 Mo 3 O 12 thin film also grows as the annealing temperature increases. The resulting orthorhombic In 0.5 Sc 1.5 Mo 3 O 12 thin films exhibit anisotropic NTE. Its volumetric coefficient of thermal expansion (CTE) is −3.44 × 10−6 °C−1, while the CTEs in a -, b - and c -axis directions are −4.70 × 10−6 °C−1, 5.37 × 10−6 °C−1, and -4.10 × 10−6 °C−1 in 25–700 °C, respectively. In addition, the transmittance of orthorhombic In 0.5 Sc 1.5 Mo 3 O 12 thin films post-annealed at 750 °C is around 87.75 %–95.03 %. [ABSTRACT FROM AUTHOR]

Orthorhombic In 0.5 Sc 1.5 Mo 3 O 12 nanofibers were prepared by electrospinning followed by a heat treatment. The effects of post-annealing temperatures on the phase composition, microstructure and morphology were investigated by XRD, SEM, HRTEM and XPS. Negative thermal expansion (NTE) behaviors of the In 0.5 Sc 1.5 Mo 3 O 12 nanofibers were analyzed by high-temperature XRD. Results indicate that the as-prepared In 0.5 Sc 1.5 Mo 3 O 12 nanofibers show an amorphous structure with smooth and homogeneous shape. The average diameter of the as-prepared In 0.5 Sc 1.5 Mo 3 O 12 nanofibers is around 515 nm. Well crystallized orthorhombic In 0.5 Sc 1.5 Mo 3 O 12 nanofibers could be prepared after post-annealing at 550 °C for 2 h with an average diameter of about 192 nm. The crystallinity of In 0.5 Sc 1.5 Mo 3 O 12 nanofibers gradually improved with the increase of annealing temperature. However, too high post-annealing temperature leads to a damage of sample's fiber structure. The high-temperature XRD results reveal that In 0.5 Sc 1.5 Mo 3 O 12 nanofibers show an anisotropic NTE, and the coefficients of thermal expansion (CTEs) along a -axis and c -axis were −5.95 × 10−6 °C−1 and -3.54 × 10−6 °C−1, while the one along b -axis is 5.61 × 10−6 °C−1. The volumetric CTE of In 0.5 Sc 1.5 Mo 3 O 12 nanofibers is −3.90 × 10−6 °C−1 and the linear one is 1.3 × 10−6 °C−1 in 25–700 °C. [ABSTRACT FROM AUTHOR]