Abstract: Nano-sized and single phase W-type hexaferrite (BaCo2Fe16O27) powders synthesized by sol–gel autocombustion method have been investigated. The samples were sintered in a temperature range of 1000–1200°C for 5h. The thermal decomposition behavior of as-prepared powder was studied by thermogravimetry (TG), differential thermal analysis (DTA) and infrared spectra (IR). The structural and magnetic properties of powders were investigated by X-ray diffraction (XRD) and vibrating sample magnetometer (VSM). The grain size calculated by Scherer equation was found in the range of 36–47nm which is small enough to obtain a suitable signal-to-noise ratio in high density recording media. Hysteresis loop measurements show that the coercivity values lie in the range of 210.61–1602.6Oe with increasing sintering temperature. Magnetization studies show a significant increase in the values from 15 to 22emu/g. The dc electrical resistivity is observed to decrease up to a certain value as the temperature increases and then rises at higher temperature. [Copyright &y& Elsevier]

Abstract: Lanthanum doped W-type hexaferrites BaZn2La x Fe16−x O27 (x =0, 0.2, 0.4, 0.6, 0.8, 1.0) were synthesized by co-precipitation and sintered at 1320°C. The X-ray diffraction reveals W-type hexagonal structure with few traces of secondary phase. The decrease in grain size as a function of La-concentration is attributed to the fact that La acts as a grain inhibitor. The saturation magnetization and remanance decrease due to spin canting on B-sites. The increase in coercivity follows 1/r behavior where r is the radius of grain. The DC resistivity was observed to increase from 0.59×107 to 8.42×107 Ωcm with increasing La-contents due to the unavailability of Fe3+ ions. This enhancement in resistivity makes these materials promising candidates for use at high frequencies in order to reduce eddy current losses. [Copyright &y& Elsevier]

Abstract: A series of BaHo x Fe16−x O27 (x =0.0, 0.2, 0.4, 0.6, 0.8, 1.0) W-type hexagonal ferrites were prepared by co-precipitation technique at high annealing temperature of 1320°C. XRD reveals single W-type hexagonal phase in these ferrites. The grain size is measured by SEM analysis using line intercept method. Saturation magnetization, retentivity and coercivity were measured from MH-loops taken on VSM. It was observed that magnetization increases with the increase of Ho content due to difference in ionic radii of Ho3+ (0.901Å) and Fe3+ (0.67Å) ions. Room temperature dc resistivity increases as a function of Ho3+ that may be due to separation between grains. The dc electrical resistivity decreases as a function of temperature which indicates the semi-conducting behavior of the samples. [Copyright &y& Elsevier]