Search

Abstract This study aimed to obtain ceramic filters with bactericidal action for water disinfection. For this, aqueous suspensions of montmorillonite K10 clay were prepared at concentrations of 48%, 50%, and 52%. Later, these were impregnated into polymeric sponges in order to form the ceramic skeletons by using the replica technique. The ceramic filters were submerged in nickel resins doped with 0.25 and 0.50 mol% silver. These resins were obtained by the Pechini method and heat-treated at 600 and 700 ºC for 2 h. Moreover, techniques such as X-ray diffraction, particle size analysis, scanning electron microscopy, energy dispersive spectroscopy, compressive strength, water absorption, and apparent porosity were used to characterize the filters, and their performance was analyzed by a bactericidal test. The bactericidal test results showed that the filters impregnated with the resin containing 0.50 mol% of silver promoted the total elimination of the Staphylococcus aureus and Escherichia coli bacteria.

Copyright of Ceramica is the property of Associacao Brasileira de Ceramica and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

Em diversas aplicações as cerâmicas celulares são submetidas a tensões térmicas severas, tal como na filtração de metais fundidos. Contudo, há poucos estudos sobre o desempenho ao choque térmico destes materiais. Uma das razões é que a metodologia para análise desta classe de materiais deve ser distinta daquela utilizada para os materiais cerâmicos densos. Isto porque no caso dos materiais celulares para filtração de metais fundidos o meio causador do choque térmico infiltra-se rapidamente na estrutura reticular de poros, reduzindo o gradiente de temperatura entre a superfície externa e a do interior do corpo. Neste contexto, a proposta do presente trabalho é verificar os efeitos de algumas propriedades dos filtros cerâmicos em seu comportamento mecânico durante testes de choque térmico em água. As propriedades consideradas são a permeabilidade, a condutividade térmica e a área superficial específica dos filtros. Para isto foram utilizados os filtros cerâmicos do sistema de Al2O3-SiC de 8, 10, 20 e 30 ppi (poros por polegada linear).In many applications, open-cell ceramics are expected to undergo severe thermal stresses, for instance, in their use as molten metal filters. However, only a few studies have considered the thermal shock behavior of these materials. One of the main reasons is the theoretical approach used for dense ceramics which may not be valid for porous materials. In this context, the aim of this work is to analyze the effects of permeability, specific surface area and thermal conductivity on the mechanical behavior of ceramic filters subjected to water quenching tests. Al2O3-SiC filters with nominal cell sizes, expressed as the number of pores per linear inch (ppi), ranged from 8 to 30 ppi were used in the experimental tests.

Este trabalho propõe a preparação de filtros cerâmicos macroporosos pela técnica da impregnação de espumas de poliuretano e utilização de uma resina preparada pelo método Pechini contendo íons alumínio e manganês como ligante. Nas temperaturas inferiores à de combustão da resina a parte orgânica age com ligante. Após a decomposição térmica, o produto da combustão, ou seja, alumina contendo íons Mn, passa a ser um ligante inorgânico mas apresentando composição química semelhante à do filtro. Os filtros assim preparados apresentaram três famílias de distribuições de tamanho de poros (50,2 e 0,2 mm) e a densidade da estrutura do material, considerando-se apenas a porosidade referente as duas últimas distribuições, é de 87% da densidade teórica.This work proposes the utilization of a resin prepared via the Pechini method, bearing aluminum and manganese cations as binders. The filters prepared in this way present three families of pore size distributions (50, 2 and 0.2 mm) and the resulting density of the material, considering only the apparent porosity of the last two distributions is 87% of the theoretical density.