As a powerful protocol for the preparation of common polymers, such as polyolefins, polyesters, and polycarbonates, late-transition-metal-catalyzed polymerization can be carried out by controlling the reaction conditions or developing dynamic catalytic systems that use external stimuli to influence the performance of the active sites, resulting in well-defined polymeric materials. In particularly, under the latter conditions, 'one catalyst' can provide more than one kind of polymer with a controlled sequence from the monomer mixture, making full use of the prepared catalyst. In this review, tunable modes, including reaction conditions, redox, light or electrochemical properties, Lewis acids, and alkali metal cations, of late-transition-metal-complex (especially iron, cobalt, and nickel)-catalyzed polymerization were collected and thoroughly discussed. [ABSTRACT FROM AUTHOR]

Five examples of bis(arylimino)tetrahydrocyclohepta[b]pyridine dichloroiron(II) complex, [2-{(Ar)N=CMe}-9-{N(Ar)}C10H10N]FeCl2 (Ar = 2-(C5H9)-4,6-(CHPh2)2C6H2Fe1, 2-(C6H11)-4,6-(CHPh2)2C6H2Fe2, 2-(C8H15)-4,6-(CHPh2)2C6H2Fe3, 2-(C12H23)-4,6-(CHPh2)2C6H2Fe4, and 2,6-(C5H9)2-4-(CHPh2)C6H2Fe5), incorporating ortho-pairings based on either benzhydryl/cycloalkyl (ring sizes ranging from 5 to 12) or cyclopentyl/cyclopentyl groups, have been prepared in reasonable yield by employing a simple one-pot template strategy. Each complex was characterized by FT-IR spectroscopy, elemental analysis, and for Fe3 and Fe5 by single crystal X-ray diffraction; pseudo-square pyramidal geometries are a feature of their coordination spheres. On treatment of Fe1–Fe5 with modified methylaluminoxane (MMAO) or methylaluminoxane (MAO), a range in catalytic activities for ethylene polymerization were observed with benzhydryl/cyclopentyl-containing Fe1/MMAO achieving the maximum level of 15.3 × 106 g PE mol−1 (Fe) h−1 at an operating temperature of 70 °C. As a key trend, the activity was found to drop as the ortho-cycloalkyl ring size increased: Fe1C5H9/CHPh2~Fe5C5H9/C5H9 > Fe2C6H11/CHPh2 > Fe3C8H15/CHPh2 > Fe4C12H23/CHPh2. Furthermore, strictly linear polyethylenes (Tm > 126 °C) were formed with molecular weights again dependent on the ortho-cycloalkyl ring size (up to 55.6 kg mol−1 for Fe1/MAO); narrow dispersities were a characteristic of all the polymers (Mw/Mn range: 2.3–4.7), highlighting the well-controlled nature of these polymerizations. [ABSTRACT FROM AUTHOR]