Search

In order to reduce the overall system cost, the development of inexpensive, high-performance and durable oxygen reduction reaction (ORR)N, Fe-codoped carbon-based (Fe/N/C) electrocatalysts to replace currently used Pt-based catalysts has become one of the major topics in research on fuel cells. This review paper lays the emphasis on introducing the progress made over the recent five years with a detailed discussion of recent work in the area of Fe/N/C electrocatalysts for ORR and the possible Fe-based active sites. Fe-based materials prepared by simple pyrolysis of transition metal salt, carbon support, and nitrogen-rich small molecule or polymeric compound are mainly reviewed due to their low cost, high performance, long stability and because they are the most promising for replacing currently used Pt-based catalysts in the progress of fuel cell commercialization. Additionally, Fe-base catalysts with small amount of Fe or new structure of Fe/Fe3C encased in carbon layers are presented to analyze the effect of loading and existence form of Fe on the ORR catalytic activity in Fe-base catalyst. The proposed catalytically Fe-centered active sites and reaction mechanisms from various authors are also discussed in detail, which may be useful for the rational design of high-performance, inexpensive, and practical Fe-base ORR catalysts in future development of fuel cells. [ABSTRACT FROM AUTHOR]

Nitrogen-doped ordered mesoporous carbon was synthesized by using polyaniline as the carbon source and SBA-15 as the template. The microstructure, composition and electrochemical behavior were extensively investigated by the nitrogen sorption isotherm, X-ray photoelectron spectroscopy, cyclic voltammetry and rotating ring-disk electrode. It is found that the pyrolysis temperature yielded a considerable effect on the pore structure, elemental composition and chemical configuration. The pyrolysis temperature from 800 to 1100 °C yielded a volcano-shape relationship with both the specific surface area and the content of the nitrogen-activated carbon. Electrochemical tests showed that the electrocatalytic activity followed a similar volcano-shape relationship, and the carbon catalyst synthesized at 1000 °C yielded the best performance. The post-treatment in NH3 was found to further increase the specific surface area and to enhance the nitrogen doping, especially the edge-type nitrogen, which favored the oxygen reduction reaction in both acid and alkaline media. The above findings shed light on electrocatalysis and offer more strategies for the controllable synthesis of the doped carbon catalyst. [ABSTRACT FROM AUTHOR]

It is of increasing interest and an important challenge to develop highly efficient less-expensive cathode catalysts for anion-exchange membrane fuel cells (AEMFCs). In this work, we have directly prepared a carbon-supported CoS nanocatalyst in a solvothermal route and investigated the effect of heat-treatment on electrocatalytic activity and long-term stability using rotating ring-disk electrode (RRDE). The results show that the heat-treatment below 400 °C under nitrogen atmosphere significantly enhanced the electrocatalytic performance of CoS catalyst as a function of annealed temperature in terms of the cathodic current density, the half-wave potential, the HO2- product and the number of electrons transferred. The CoS catalyst that annealed at 400 °C (CoS-400) has exhibited a promising performance with the half-wave potential of 0.71 V vs. RHE (the highest one for non-precious metal chalcogenides), the minimum HO2- product of 4.3% at 0.60 V vs. RHE and close to the 4-electron pathway during the oxygen reduction reaction in 0.1 M KOH. Also, the CoS-400 catalyst has comparable durability to the Pt/C catalyst. [ABSTRACT FROM AUTHOR]

The carbon supported iron selenide catalysts (FeSe2/C) were prepared with various selenium to iron ratios (Se/Fe), namely, Se/Fe = 2.0, 2.5, 3.0, 3.5 and 4.0, through facile microwave route by using ferrous oxalate (FeC2O4⋅2H2O) and selenium dioxide (SeO2) as precursors. Accordingly, effects of Se/Fe ratio on the crystal structure, crystallite size, microstructure, surface composition and electrocatalytic activity for oxygen reduction reaction (ORR) of FeSe2/C in an alkaline medium were systematically investigated. The results revealed that all the FeSe2/C catalysts obtained with the Se/Fe ratios of 2.0-4.0 exhibited almost pure orthogonal FeSe2 structure with the estimated mean crystallite sizes of 32.9-36.2 nm. The electrocatalytic activities in potassium hydroxide solutions were higher than those in perchloric acid solutions, and two peak potentials or two plateaus responded to ORR were observed from cyclic voltammograms and polarization curves, respectively. The ORR potentials of 0.781-0.814 V with the electron transfer numbers of 3.3-3.9 at 0.3 V could be achieved as the Se/Fe ratios varied from 2.0 to 4.0. The Fe and Se were presented at the surface of FeSe2/C upon further reduction on FeSe2. The Se/Fe ratios slightly influenced the degree of graphitization in carbon support and the amount of active sites for ORR. [ABSTRACT FROM AUTHOR]

The goal of this research was to synthesize activated nitrogen-doped nanocarbons with high specific surface area and adjustable pore size distribution using wood charcoal as a raw material. The resulting carbon materials were tested for possible application as oxygen reduction reaction catalysts in alkaline media. Activated carbons were obtained using a thermochemical activation method with NaOH. Nitrogen was introduced into activated carbons using dicyandiamide solution. It was demonstrated that the content of introduced nitrogen depends on oxygen content in the structure of the activated carbon. The oxygen reduction reaction activity of the activated and nitrogen-doped carbon material was comparable with a commercial 20% Pt/C catalyst. Electrocatalytic properties of the synthesized N-doped wood-derived carbon catalysts may be associated with the highly developed surface area, specific ratio of micro- and mesopores, as well as the high percentage of pyridinic nitrogen. [ABSTRACT FROM AUTHOR]