Mono metallic and bimetallic Pd (1 wt. %)&ndash, Au (3 wt. %) catalysts were prepared using two ceria supports doped with 1 wt. % Y2O3. Yttrium was added by impregnation or co-precipitation. The catalyst synthesis was carried out by deposition&ndash, precipitation method, with sequential deposition&ndash, precipitation of palladium over previously loaded gold in the case of the bimetallic samples. The obtained materials, characterized by X-ray powder diffraction (XRD), High resolution transmission electron microscopy (HRTEM), X-ray photoelectron spectroscopy (XPS), and temperature programmed reduction (TPR) techniques, were tested in the complete benzene oxidation (CBO). The results of the characterization analyses and the catalytic performance pointed to a close relationship between structural, redox, and catalytic properties of mono and bimetallic catalysts. Among the monometallic systems, Pd catalysts were more active as compared to the corresponding Au catalysts. The bimetallic systems exhibited the best combustion activity. In particular, over Pd&ndash, Au supported on Y-impregnated ceria, 100% of benzene conversion towards total oxidation at the temperature of 150 &deg, C was obtained. Comparison of surface sensitive XPS results of fresh and spent catalysts ascertained the redox character of the reaction.

Gold (3 wt. %) catalysts on Y-doped (1, 2.5, 5 and 7.5 wt. % Y2O3) ceria supports prepared by coprecipitation (CP) or impregnation (IM) were studied in complete benzene oxidation (CBO). A low-extent Y modification was chosen to avoid ordering of oxygen vacancies. The samples were characterized by XRD, TGA, XPS and TPR techniques. A positive role of air pretreatment at 350 °C as compared to 200 °C was established for all Y-containing catalysts and it was explained by cleaning the active sites from carbonates. The oxygen supply cannot be considered as a limiting step for benzene oxidation except for the high 7.5%-doped samples, as suggested by TGA and TPR data. On the basis of XPS results of fresh and used in CBO catalysts, the presence of cationic gold species does not seem important for high CBO activity. The gold catalyst on an IM support with 1% Y-doping exhibited the best performance. A 100% benzene conversion was achieved only over this catalyst and Au/ceria, while it was not reached even at 300 °C over all other studied catalysts. Gold and ceria particle agglomeration or coke formation should be excluded as a possible reason, and the most probable explanation could be associated with the importance of the benzene activation stage.