A novel composite membrane consisting of an activated carbon membrane with filamentous carbon, applicable to water treatment, was fabricated by a combination of conventional carbonization and thermal deposition. The carbonization was performed after dipping a ceramic support in a latex polymer followed by the application of ferric sulfate [Fe2(SO4)3·nH2O] catalyst. This was followed by CVD from methane at 1050–1100 °C. The resulting membrane therefore consisted of a filamentous carbon layer grown with a combination of the catalyst and deposited hydrocarbon, and an activated carbon layer on a ceramic support. These structural characteristics were confirmed by means of the cut-off of dextran molecules, the pure water permeability, SEM, and the adsorption of phenol. Water treatment experiments using phenol and poly(methyl methacrylate) as model pollutants indicated that this membrane was able to remove dissolved organics of low molecular weight and suspended solids. Also, the filamentous carbon layer successfully prevented the fine particles from sticking on the external surface of the membrane by frequent back washing. [Copyright &y& Elsevier]

Abstract: A double-sided surface light source based on field emission (FE) using an alternating current power source is demonstrated. Carbon-nanotube (CNT) emitters and ZnS phosphor are mixed and screen-printed onto two pieces of indium tin oxide glass that were assembled together with the coated surfaces facing each other to make a parallel-plate, diode-structure FE device. The device has a double-sided luminance distribution with a turn-on field of 2V/μm, a good uniformity, and a stable luminance of 4000cd/m2. The results show that CNTs not only act as good field emitters but also as an electrically conductive network around the isolated phosphors. The network prevents electric arcing and thus extends the lifetime of the device. [Copyright &y& Elsevier]

Abstract: Thin-walled carbon nanotubes (TWCNTs) were synthesized using a zirconium (Zr) plate by cold-wall chemical vapor deposition of a mixture gas consisting of C2H2 and H2 under a pressure of 1.20torr. The Zr plate was used for the formation of Zr nanocatalysts during the thermal process and used as substrate to eliminate the effects of interactions between catalyst and substrate during CNT synthesis. The TWCNTs were 4–9nm in diameter and a few micrometers long. Nanometer-sized defects on the Zr bulk material may have a low melting temperature, allowing them to form droplet-like catalysts and achieve high carbon solubility for the formation of CNTs. [Copyright &y& Elsevier]