Nanocelluloses were prepared from sugarcane bagasse celluloses by dynamic high pressure microfluidization (DHPM), aiming at achieving a homogeneous isolation through the controlling of shearing force and pressure within a microenvironment. In the DHPM process, the homogeneous cellulose solution passed through chambers at a higher pressure in fewer cycles, compared with the high pressure homogenization (HPH) process. X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) demonstrated that entangled network structures of celluloses were well dispersed in the microenvironment, which provided proper shearing forces and pressure to fracture the hydrogen bonds. Gel permeation chromatography (GPC), CP/MAS 13 C NMR and Fourier transform infrared spectroscopy (FT-IR) measurements suggested that intra-molecular hydrogen bonds were maintained. These nanocelluloses of smaller particle size, good dispersion and lower thermal stability will have great potential to be applied in electronics devices, electrochemistry, medicine, and package and printing industry. [ABSTRACT FROM AUTHOR]

Abstract: Nanocellulose from sugarcane bagasse was isolated by high pressure homogenization in a homogeneous media. Pretreatment with an ionic liquid (1-butyl-3-methylimidazolium chloride ([Bmim]Cl)) was initially involved to dissolve the bagasse cellulose. Subsequently, the homogeneous solution was passed through a high pressure homogenizer without any clogging. The nanocellulose was obtained at 80MPa for 30 cycles with recovery of 90% under the optimum refining condition. Nanocellulose had been characterized by Fourier transformed infrared spectra, X-ray diffraction, thermogravimetric analysis, rheological measurements and transmission electron microscopy. The results showed that nanocellulose was 10–20nm in diameter, and presented lower thermal stability and crystallinity than the original cellulose. The developed nanocellulose would be a very versatile renewable material. [Copyright &y& Elsevier]