Search

This study evaluated the physicochemical, biological, and antimicrobial properties of a new hydraulic calcium silicate-based modified material, and compared it with MTA Repair HP and MTA Angelus. The materials were assessed regarding color luminosity (L), color change, radiopacity, setting time, and ISO 6876:2012 linear flow. Volumetric filling and volume change were evaluated using microcomputed-tomography (µCT). Chemical characterization after 28 days in Hank's Balanced Salt Solution (HBSS) and pH analysis were also assessed. Biological characterization of cytotoxicity and microbiological assessment were also undertaken. Shapiro-Wilk, ANOVA, Levene and post hoc analyses with Bonferroni correction were performed, adopting a 5% significance level (p <0.05). Bio-C Pulpo exhibited the highest L values after 90 days. All tested materials demonstrated color change during the analyses, and had radiopacity above 5 mm Al. MTA Repair HP set faster than Bio-C Pulpo, whereas the latter had the highest linear flow. MTA Repair HP had the highest volumetric filling in µCT analysis. Bio-C Pulpo showed the highest alkalinity during all tested periods, and the highest volumetric loss (above 9%), in comparison with MTA Repair HP and MTA Angelus. Bio-C Pulpo did not form calcium hydroxide after hydration. MTA Repair HP demonstrated the highest cytocompatibility, and Bio-C Pulpo, the highest cytotoxicity. No inhibition halos were observed for any material, and similar higher turbidity values were seen after direct contact. Composition additives used in Bio-C Pulpo modified its properties, and both the absence of calcium hydroxide deposition after hydration, and the related cytotoxicity of this material are of particular concern.

Ca3SiO5 is new cement based on the composition of Portland that has been developed to have superior physicochemical and biological properties. In a clinical evaluation, the cement did not appear to have cytotoxic properties and allowed for the proliferation of pulp cells and gingival fibroblasts. However, no previous studies have evaluated the genotoxicity or the mutagenicity of Ca3SiO5in vivo. Therefore, the goal of this study is to evaluate the genotoxic and mutagenic potential of Ca3SiO5-based cement in vivo. Twenty-four male Wistar rats were divided into 3 groups (n = 8). Group A rats received subcutaneous implantation of Ca3SiO5 in the dorsum. Group B rats received a single dose of cyclophosphamide (positive control). Group C rats received subcutaneous implantation of empty tubes in the dorsum (negative control). After 24 hours, all animals were euthanized and the bone marrow of the femurs was collected for use in the comet assay and the micronucleus test. The comet assay revealed that the Ca3SiO5 group had a tail intensity of 23.57 ± 7.70%, the cyclophosphamide group had a tail intensity of 27.43 ± 7.40%, and the negative control group had a tail intensity of 24.75 ± 5.55%. The average number of micronuclei was 6.25 (standard deviation, SD = 3.53) in the Ca3SiO5 group, 9.75 (SD = 2.49) in the cyclophosphamide group, and 0.75 (SD = 1.03) in the negative control group. There was an increase in the micronuclei frequency in the Ca3SiO5 group compared to that of the negative control group (p < 0.05). Our data showed that exposure to the Ca3SiO5-based cement resulted in an increase in the frequency of micronuclei, but no genotoxicity was detected according to the comet assay.

Several calcium silicate-based biomaterials have been developed in recent years, in addition to Mineral Trioxide Aggregate (MTA). The aim of this study was to evaluate the cytotoxicity, genotoxicity and apoptosis/necrosis in human osteoblast cells (SAOS-2) of pure calcium silicate-based cements (CSC) and modified formulations: modified calcium silicate-based cements (CSCM) and three resin-based calcium silicate cements (CSCR1) (CSCR 2) (CSCR3). The following tests were performed after 24 hours of cement extract exposure: methyl-thiazolyl tetrazolium (MTT), apoptosis/necrosis assay and comet assay. The negative control (CT-) was performed with untreated cells, and the positive control (CT+) used hydrogen peroxide. The data for MTT and apoptosis were submitted to analysis of variance and Bonferroni's posttest (p < 0.05), and the data for the comet assay analysis, to the Kruskal-Wallis and Dunn tests (p < 0.05). The MTT test showed no significant difference among the materials in 2 mg/mL and 10 mg/mL concentrations. CSCR3 showed lower cell viability at 10 mg/mL. Only CSC showed lower cell viability at 50 mg/mL. CSCR1, CSCR2 and CSCR3 showed a higher percentage of initial apoptosis than the control in the apoptosis test, after 24 hours exposure. The same cements showed no genotoxicity in the concentration of 2 mg/mL, with the comet assay. CSC and CSCR2 were also not genotoxic at 10 mg/mL. All experimental materials showed viability with MTT. CSC and CSCR2 presented a better response to apoptosis and genotoxicity evaluation in the 10 mg/mL concentration, and demonstrated a considerable potential for use as reparative materials.

The present study aimed at evaluating the cytotoxic effects of a novel cement called CER on periodontal fibroblast-like cells of mice (MDPL-20), in comparison with different formulations of Mineral Trioxide Aggregate (MTA), by means of the cell viability test (MTT) and cell morphology analysis. Thirty-two round-shaped samples were fabricated with the following cements: white MTA, white and gray CER and experimental white MTA. The samples were immersed in serum-free culture medium for 24 hours or 7 days (n = 16). The extracts (culture medium + components released from the cements) were applied for 24 hours to previously cultured cells (40.000 cells/cm2) in the wells of 24-well plates. Cells seeded in complete culture medium were used as a negative control. Cell viability was assessed using the MTT assay. Two samples of each cement were used for cell morphology analysis by Scanning Electron Microscopy (SEM). The extracts obtained at the 7-day period presented higher cytotoxicity compared with the 24-hour period (p < 0.05). The gray CER obtained at 24 hours presented the highest cytotoxic effect, whereas the experimental white MTA presented the lowest, similar to the control (p > 0.05). However, at the 7-day period, the experimental white MTA presented no significant difference in comparison with the other cements (p > 0.05). At the 7-day period, CER cement presented cytotoxic effects on fibroblast-like cells, similar to different MTA formulations. However, the immersion period in the culture medium influenced the cytotoxicity of the cements, which was greater for CER cement at 24 hours.

Recently, regular and white mineral trioxide aggregate (MTA) are being used in Dentistry as retrofilling materials. Genotoxicity and cytotoxicity tests form an important part of cancer research and risk assessment of potential carcinogens. Thus, the goal of this study was to examine the genotoxicity and cytotoxicity of regular and white MTA in vitro by the single cell gel (comet) assay and trypan blue exclusion test, respectively. Mouse lymphoma cells were exposed to two presentation forms of MTA at final concentrations ranging from 1 to 1,000 microg/mL for 3 h at 37 degrees C. The results showed that both compounds tested did not produce genotoxic effects at all concentrations evaluated. Likewise, no statistically significant differences (p > 0.05) were observed in cytotoxicity. Taken together, our results suggest that regular and white MTA are not genotoxins and are not able to interfere in cellular viability as assessed by single cell gel (comet) assay and trypan blue assay, respectively.