This study evaluated the cytotoxic effect and the ability to inhibit matrix metalloproteinases (MMP-2 and MMP-9) of 0.2% chitosan (CH) and 1% acetic acid (AA) compared with 17% ethylenediaminetetraacetic acid (EDTA). Cell viability assay was performed according to ISO 10993-5 with mouse fibroblasts (L929). The culture was exposed to 0.2% CH, 1% AA, and 17% EDTA. The chelating agents were evaluated immediately after contact with the cells and after 6 h, 12 h, and 24 h of incubation. Cell viability was analyzed using the 3-(4,5-dimethythiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay. Inhibition of the gelatinolytic activity of MMP-2 and MMP-9 was evaluated by gelatin zymography. Different concentrations of CH were evaluated: 50 mM, 5 mM, 0.5 mM, and 0.05 mM. EDTA (0.5 mM) was used as a positive control. The results demonstrated that CH and AA had an initial cytotoxic effect, which decreased after 6 h, 12 h, and 24 h, being statistically similar to EDTA (P > 0.05). Additionally, CH at concentrations of 50 mM, 5 mM, and 0.5 mM had an inhibitory effect on MMP-2 and MMP-9, similar to that of the control with EDTA. The chelating agents had no cytotoxic effects after 24 h. MMP-2 and MMP-9 were inhibited by the experimental solutions.

The aim of this study was to evaluate of pre-heating, filler contents and ceramic thickness on film thickness, microshear bond strength, degree of conversion and color change on ceramic veneers. Two experimental composites were prepared (Bis-GMA/UDMA/BisEMA/ TEGDMA), with different amounts of filler (65% or 50%wt) simulating a conventional and a flowable composite. The flowable (F) was used at room temperature and, the conventional either at room temperature (C) or pre-heated (CPH). Disk-shaped ceramics with different thickness (0.4 mm, 0.8 mm, 1.5 mm) were prepared. The film thickness was evaluated according to the ISO 4049 (n=10). The microshear bond strength (n=10) was evaluated in enamel using tubing specimens light-cured through the ceramic veneer. The degree of conversion was evaluated using Raman spectroscopy. The color change of the ceramic restorations (n=10) was evaluated by spectrophotometry. The results were submitted to 2-way ANOVA and Tukey's post hoc test (a=5%). For the film thickness 1-way ANOVA was used (a=5%). The C presented the thicker film thickness; the CPH produced a similar film thickness in comparison to the F. All composites showed similar microshear bond strength. The degree of conversion of the F was higher than the C and CPH. The degree of conversion of the composites photo-activated through a 0.4 mm was higher than the composites photo-activated through thicker ceramics. The C showed the highest color change, while the CPH showed similar color change to the F. In conclusion, pre-heated conventional composites seem to be a potential alternative to lute ceramic veneers such as the flowable composites.