Search

The basic thermophysical properties of oriented strand boards were determined experimentally for use in humid conditions (OSB3) depending on the moisture content. The dependency between the thermal conductivity, thermal diffusivity, specific heat capacity, and the moisture content in the range of 0% to 10%, was examined. The non-stationary extended dynamic plane source (EDPS) experimental method was used. EDPS method was modified for anisotropic materials, i.e. with special considerations of heat-loss effect occurring at the edge of measuring samples, finite geometry of the sample and orthotropic thermal conductivity, for use with anisotropic materials. The validity of the experimental method was verified on polymethylmethacrylate (PMMA) samples. The error rate of measurements conducted on PMMA samples was less than 3%, and for OSB3 boards it was less than 5.5%. Based on the experimental results, regression equations of the dependency between the monitored properties and the moisture content were determined. In the case of thermal conductivity and thermal capacity, the determined dependencies showed a high correlation rate.

A barrier plasma, created at atmospheric pressure, was used to improve the surface and adhesive properties of polyester (PES) film with respect to wood using polyurethane adhesives. The modification of PES film surfaces using barrier discharge plasma is attractive for various applications. Plasma pre-treatment initiates and participates in grafting, polymerization, or cross-linking reactions on the PES surface. This method of surface modification is clean, dry, ecological, and very efficient. The enhancement of the wettability of the polyester film was necessary for promoting higher adhesion to wood with water-based adhesives. The treatment of polyester films by barrier plasma led to a considerable increase in the surface free energy of the film and subsequently an increase in the peel strength of the adhesive joint of PES film-oak wood with polyurethane adhesive. The authors are grateful for the financial support of the Ministry of Education of the Slovak Republic and Slovak Academy of Sciences, projects VEGA 2/0199/14 and 1/0626/16, and the Slovak Research and Development Agency under the contracts No. APVV-14-0566 and APVV-14-0506. Scopus

Mechanical separators and fabric filters are being used to remove airborne fine particles generated during the processing and handling of wood. Such particles might have a harmful effect on employee health, not only in small- but also in large-scale wood processing facilities. The amount of wood dust and its dispersion conditions vary according to geometric boundary conditions. Thus, the dispersion conditions could be changed by changing the linear size of the particles. Moreover, the smaller the particles are, the more harmful they can be. It is necessary to become familiar with properties, from a health point of view, of wood dust generated from processing. Wood dust has to be sucked away from the processing area. The fractional separation efficiency of wood dust can be improved using exhaust and filtering devices. Filtration efficiency depends on moisture content, particle size, and device performance. Because of the carcinogenicity of wood dust, the concentration of wood dust in air has to be monitored regularly. Based on the results hereof, a conclusion can be made that both mechanical separators of types SEA and SEB as well as the fabric filters with FINET PES 1 textile are suitable for the separation of wet saw dust from all types of wooden waste produced within the process.