Search

Consecutive superheated steam-alkali treatment was introduced to modify oil palm mesocarp fiber (OPMF) prior to biocomposite fabrication. The biocomposite made up of 70 wt.% modified OPMF (SNOPMF) and 30 wt.% poly(butylene succinate) (PBS) was prepared by melt blending followed by compression molding. A silane coupling agent of 3-aminopropyltrimethoxysilane (APTMS) was also incorporated into the SNOPMF/PBS biocomposite during the compounding process to impart better adhesion at the SNOPMF-PBS interface. The experimental results revealed that the tensile, flexural, and impact strengths were enhanced by 16, 30, and 15%, respectively, after the introduction of 2 wt.% APTMS to the SNOPMF/PBS biocomposite. Similarly, the resistance to water uptake and thickness swelling of this biocomposite was improved by 34 and 49%, respectively, relative to SNOPMF/PBS biocomposite. The SEM observation of the tensile fracture surface showed that APTMS improved the interfacial adhesion between SNOPMF and PBS. Based on the results, it can be deduced that APTMS could be a good coupling agent for improving the SNOPMF-PBS adhesion and, thereby, lead to a water resistant biocomposite of enhanced mechanical properties.

In this work, the surface of oil palm mesocarp fiber (OPMF) was modified via alkaline-peroxide treatment with hydrogen peroxide under alkaline conditions. The effect of the treatment on the chemical composition and microstructure of the fiber was examined using chemical analysis, Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), and X-ray diffraction (XRD) analysis. The treatment resulted in the removal of lignin, hemicellulose, and waxy substances from the fiber and increased its surface roughness and crystallinity. The eco-friendly biocomposite was made from poly(butylene succinate) (PBS) and chemically treated fiber at a weight ratio of 30:70, and was fabricated via a melt-blending technique followed by hot-pressed moulding. The results indicated that alkaline-peroxide treatment of the fiber improved the tensile strength, tensile modulus, and elongation at break of the OPMF/PBS biocomposite by 54, 830, and 43%, respectively. The SEM analysis revealed improvement of the interfacial adhesion between the chemically treated fiber and the PBS. This work demonstrates that alkaline-peroxide treatment of fiber is beneficial prior to its use in fabricating biocomposites.

In this work, oil palm mesocarp fiber (OPMF) was surface-treated with varying NaOH concentrations (1, 3, 5, 7, or 9%) and soaking times (1, 2, 3, or 4 h) at room temperature aiming to enhance its adhesion to the thermoplastic matrix for biocomposite application. The biocomposites from alkali treated OPMFs and poly(butylene succinate) at weight ratios of 70:30 were fabricated by a melt blending technique and hot-pressed moulding. The results indicate that NaOH treatment removed fiber’s surface waxes, hemicellulose, and lignin, and produced fiber with rough surface morphology. The tensile results showed that OPMF treated in 5% NaOH solution for 3 h produced biocomposite with enhanced tensile strength (30%), tensile modulus (105%), and elongation at break (16%), as well as reduced water absorption (15%) and thickness swelling (13%) in comparison to that of untreated OPMF. Scanning electron microscopy showed improvement of interfacial adhesion between treated fiber and poly(butylene succinate). These results suggest that NaOH treatment could be an effective form of treatment for OPMF in biocomposites materials.

In this work, surface modifications of oil palm mesocarp fiber were carried out by using superheated steam, alkali, and consecutive superheated steam-alkali treatments, aiming at modification of fiber’s surface for biocomposite applications. The chemical compositions of fiber were modified after treatments as validated by chemical analysis and Fourier transform infrared spectroscopy. The treated fibers under microscopy observation showed relatively clean, rough, and textured surfaces due to the elimination of impurities and hemicellulose. The crystallinity index and thermal stability of treated fibers were relatively higher than that of untreated fiber as determined by X-ray diffraction and thermogravimetric analyses, respectively. A reduction in water absorption of fiber after treatments was also noted. These results indicated those treatments were effective in modifying the chemical compositions and microstructure of fiber. The treatments also increased the crystallinity and thermal stability, as well as reduced the hygroscopicity of fiber. Those treatments could increase the suitability of fiber to be used in the development of biocomposites.

In this work, oil palm mesocarp fiber (OPMF) was surface-treated with varying NaOH concentrations (1, 3, 5, 7, or 9%) and soaking times (1, 2, 3, or 4 h) at room temperature aiming to enhance its adhesion to the thermoplastic matrix for biocomposite application. The biocomposites from alkali treated OPMFs and poly(butylene succinate) at weight ratios of 70:30 were fabricated by a melt blending technique and hot-pressed moulding. The results indicate that NaOH treatment removed fiber's surface waxes, hemicellulose, and lignin, and produced fiber with rough surface morphology. The tensile results showed that OPMF treated in 5% NaOH solution for 3 h produced biocomposite with enhanced tensile strength (30%), tensile modulus (105%), and elongation at break (16%), as well as reduced water absorption (15%) and thickness swelling (13%) in comparison to that of untreated OPMF. Scanning electron microscopy showed improvement of interfacial adhesion between treated fiber and poly(butylene succinate). These results suggest that NaOH treatment could be an effective form of treatment for OPMF in biocomposites materials. [ABSTRACT FROM AUTHOR]