Xenogeneic extracellular matrices (ECMs) have been shown to be effective as naturally occurring scaffolds for soft-tissue repair. As acellular tissue substitutes at the time of surgical implantation, ECMs are subjected to the mechanical forces and micro-environmental conditions representative of the anatomical location in which they are placed. Ideally such natural scaffolds would possess mechanical properties that allow for normal tissue function in and around the implant site. The ball-burst test was used to simulate biaxial forces and to determine the strength of the ECM scaffold under a relevant physiological loading condition. The ball-burst test, in itself, does not quantify intrinsic mechanical properties and therefore a methodology was developed to determine the maximum stress resultant tangent modulus (MSRTM) or the maximum stress tangent modulus (MSTM), stress to failure (sigma(f)), failure stress resultant (N(f)), ball-burst pressure (P), and maximum elongation (lambda(max)) from the raw ball-burst data obtained at a constant-rate of transverse. The analytical methodology was compared to finite element simulations and showed good correlation with the analytical solution presented. The proposed approximations were used to compute biaxial failure properties for a variety of multilaminate ECM devices with varying number of layers, disinfection and sterilization, and organ origin.

Xenogeneic extracellular matrix (ECM) can be harvested and configured to function as a bioscaffold for tissue and organ reconstruction. The mechanical properties of the ECM vary depending upon the tissue from which it is harvested. Likewise, the manufacturing steps required to develop ECMs into medical grade devices will affect the surface morphology and the mechanical properties of the bioscaffold; important properties for constructive tissue remodeling. The present study compared the ball-burst strength of five different ECM scaffolds before and after treatment with peracetic acid (PAA): porcine small intestinal submucosa (SIS), porcine urinary bladder submucosa (UBS), porcine urinary bladder matrix (UBM), a composite of UBS + UBM, and canine stomach submucosa (SS). This study also compared the mechanical properties of 2- and 4-layer ECM scaffolds. Results showed 2-layer SS devices had the highest ball-burst value of all 2-layer ECM devices. Moreover, all 4-layer ECM devices had similar ball-burst strength except for 4-layer UBM devices which was the weakest. PAA-treatment decreased the ball-burst strength of SS and increased the ball-burst strength of UBS 2-layer devices. This study showed the material properties of the ECM scaffolds could be engineered to mimic those of native soft tissues (i.e. vascular, musculotendinous, etc) by varying the number of layers and modifying the disinfection/sterilization treatments used for manufacturing.