Cellulose nanocrystals (CNCs) are unique and promising natural nanomaterials that can be extracted from native cellulose fibers by acid hydrolysis. In this study, we developed chemically modified CNC derivatives by covalent tethering of PEGylated biotin and perylenediimide (PDI)-based near-infrared organic dye and evaluated their suitability for labeling and imaging of different cell lines including J774A.1 macrophages, NIH-3T3 fibroblasts, HeLa adenocarcinoma cells, and primary murine dendritic cells. PDI-labeled CNCs showed a superior photostability compared to similar commercially available dyes under long periods of constant and high-intensity illumination. All CNC derivatives displayed excellent cytocompatibility toward all cell types and efficiently labeled cells in a dose-dependent manner. Moreover, CNCs were effectively internalized and localized in the cytoplasm around perinuclear areas. Thus, our findings demonstrate the suitability of these new CNC derivatives for labeling, imaging, and long-time tracking of a variety of cell lines and primary cells.

Polysaccharide-structured copolymer hydrogel having excellent pH-sensitivity was developed from N,N-dimethylacrylamide (DMAc) and vinyl-functionalized Pectin (Pec). The Pec was vinyl-functionalized by way of chemical reaction with glycidyl metacrylate (GMA) in water under acidic and thermal stimuli. 13C NMR, 1H NMR, and FT-IR spectra revealed that the vinyl groups coming from the GMA were attached onto backbone of the polysaccharide. The hydrogels were obtained by polymerization of the Pec-vinyl with the DMAc. 13C-CP/MAS NMR and FTIR spectra confirmed that the gelling process occurred by way of the vinyl groups attached on Pec-vinyl backbone. The values of apparent swelling rate constant (k) decreased appreciably for pH greater than 6, demonstrating the swelling process of the hydrogel becomes slower at more alkaline conditions. There was an increase of diffusional exponent (n) with increasing pH of the surrounding liquid. This means the water absorption profile becomes more dependent on the polymer relaxation in basified swelling media. In this condition, a longer water absorption half-time (t1/2) was verified, suggesting the polymer relaxation mechanism of the hydrogel would have a considerable effect on the t1/2.