Search

In this work, copper (Cu) matrix composite reinforced with titanium carbide (TiC) was fabricated by powder metallurgy (PM) method with the varying TiC content from 0% to 12% by weight in the step of 4%. The required weight percentage of powders was milled in an indigenously developed ball milling setup. Green compacts were made using a computer-controlled hydraulic press (400 kN) and sintered in a muffle furnace at a temperature of 950°C. Scanning electron microscope (SEM) was used to analyze the distribution of TiC particles in Cu matrix in as-sintered conditions. X-ray diffraction (XRD) analysis resulted in the existence of respective phases in the produced composites. The structural characteristics such as stress, strain, dislocation density, and grain size of the milled composites were evaluated. Cold upsetting was conducted for the sintered composites at room temperature to evaluate the axial (σz), hoop (σө), hydrostatic (σm), and effective (σeff) true stresses. These stresses were analyzed against true axial strain (εz). Results showed that the increase in the inclusion of weight percentage of TiC into the Cu matrix increases density, hardness, (σz), (σө), (σm), (σeff), and stress ratio parameters such as (σz/σeff), (σθ/σeff), (σm/σeff), and (σz/σθ) of the composites.

In the current research, AA6082 aluminium alloy matrix composites (AAMCs) incorporated with various weight fractions of titanium diboride (0, 3, 6, and 9 wt%) were prepared via an in situ casting technique. The exothermic reaction between inorganic powders like dipotassium hexafluorotitanate (K2TiF6) and potassium tetrafluoroborate (KBF4) in molten Al metal contributes to the development of titanium diboride content. The manufactured AA6082-TiB2 AAMCs were evaluated using a scanning electron microscope (SEM) and X-ray diffraction (XRD). The mechanical properties and wear rate (WR) of the AAMCs were investigated. XRD guarantees the creation of TiB2 phases and proves the nonappearance of reaction products in the AMCs. SEM studies depict the even dispersion of TiB2 in the matrix alloy. The mechanical and tribological properties (MTP) of the AAMCs showed improvement by the dispersion of TiB2 particles. The WR decreases steadily with TiB2 and the least WR is seen at nine weight concentrations of TiB2/AA6082 AAMCs. Fabricated composites revealed 47.9% higher flexural strength and 14.2% superior compression strength than the base AA6082 alloy.

Aluminum, magnesium, and copper materials must have increased mechanical strength with enhanced wear and corrosion resistance. Substantial research focused on reinforcing hard particles into low-strength materials using stir casting or powder metallurgy. This work is intended to develop the magnesium hybrid matrix with the dispersion of boron carbide (B4C) and multiwall carbon nanotubes (MWCNTs). Hybrid magnesium composites are prepared, although the powder metallurgy route considers different process parameters. Statistical analysis such as Taguchi L16 orthogonal array is involved in this work. It is used to find the magnesium hybrid samples’ minimum and maximum wear, corrosion, and microhardness levels. Powder metallurgy parameters are B4C (3%, 6%, 9%, and 12%), MWCNT (0.2%, 0.4%, 0.6%, and 0.8%), ball milling (1, 2, 3, and 4 h), and sintering (3, 4, 5, and 6 h). The ball milling parameters are extremely influenced in the wear test analysis. Minimum wear losses are obtained as 0.008 g by influencing the 4 h ball milling process. Similarly, 3 h of sintering time offered a minimum corrosion rate of 0.00078 mm/yr. In microhardness analysis, the percentage of MWCNTs is highly implicated in narrow hardness resulting in the hardness value of 181. The hardness value is recorded using 0.2% MWCNTs in the magnesium alloy AZ80.

Clean technology-based natural fiber composite fabrication is the prime aim of this piece of research. Natural fibers highly replace metal usage in industries and automobile, marine, medical applications, and so on. Vast amounts of natural fibers are freely available in all areas. In this research, work nanofiller material such as nano form waste coir fiber is collected from used car seat. The 10 wt.% of nanofiller material is added to the preparation of natural nanocomposites (ramie and abaca fiber). Hybrid composites are fabricated with the influence of different process parameters, namely, fiber weight percentage (20 wt.%, 30 wt.%, 40 wt.%, and 50 wt.%), NaOH action % (4%, 6%, 8%, and 10%), compression pressure (9 MPa, 12 MPa, 15 MPa, and 18 MPa), and temperature (100°C, 120°C, 140°C, and 160°C). Furthermore, the strength of this hybrid composite has analyzed by conducting flexural, impact, and shore hardness tests. These tests have provided the influence of selected parameters and their effects on the results of experimental work. In the flexural analysis, 6% of NaOH action has offered maximum flexural strength of the specimens. Correspondingly in the impact test, 30 wt.% of fiber is produced higher impact strength. Finally, applying 15 Mpa of compression pressure records the maximum shore hardness.