Search

Optimal in vitro conditions are necessary for the development of a strong, well structured, and functional tissue engineered cardiovascular structure eventually designed for implantation. To further optimize in vitro conditions for cell proliferation and extracellular matrix formation in tissue engineering of cardiovascular structures, in this study, ascorbic acid and growth factors as additives to standard cell culture medium were evaluated for their effect on tissue development in vitro. Biodegradable polymer patches [polyglycolic acid (PGA) coated with poly-4-hydroxybutyrate (P4HB)] were seeded with human pediatric aortic cells and cultured for 7 and 28 days. Group A was cultured with standard medium (DMEM with 10% fetal calf serum and 1% antibiotics) supplemented with ascorbic acid; group B was cultured with standard medium plus ascorbic acid and basic fibroblast growth factor (bFGF); group C was cultured with standard medium adding ascorbic acid and transforming growth factor (TGF). Analysis of the cell seeded polymer constructs included DNA assay, collagen assay, and histologic and immunohistochemical examination for cell proliferation and collagen formation. After 7 and 28 days of culture, group B and group C showed a significantly higher DNA content compared with group A. The addition of bFGF (group B) led to a markedly higher collagen synthesis after 28 days of culture compared with the additives in groups C and A. The histologic and immunohistochemical examination also revealed a more dense, organized tissue development with pronounced matrix protein formation in the tissue engineered structures in group B after 28 days of culture. When seeded on to the polymeric scaffold, human vascular cells proliferate and form organized cell tissue after 28 days of culture. The addition of bFGF and ascorbic acid to the standard medium enhances cell proliferation and collagen synthesis on the biodegradable polymer, which leads to the formation of more mature, well organized tissue engineered structures.

In cardiovascular tissue engineering, synthetic or biologic scaffolds serve as templates for tissue development. Currently used scaffolds showing toxic degradation and immunogenic reactions are still far from ideal. We present a new alternative method to develop completely autologous human tissue without using any scaffold materials. Human vascular cells of arterial and venous origin were cultured to form cell sheets over a 4 week period under standard conditions. Thereafter, cell sheets of each origin were folded and cultured in a newly developed frame device for an additional 4 weeks. Controls remained under standard culture conditions. Tissue development was evaluated by morphology and biochemical assays. The formation of multilayered cell sheets and production of extracellular matrix were observed in all groups. Folded and framed neo-tissue showed a solid structure, with increased matrix formation and tissue organization when compared with the control groups. DNA content indicated significantly lower cell proliferation, and hydroxyproline assay indicated significantly higher collagen content in the framed cell sheets. We present a new approach to the engineering of cardiovascular tissue without the use of biodegradable scaffold material. Three-dimensional, completely autologous human tissue may be developed on the basis of this structure, thus avoiding scaffold induced toxic degradation or inflammatory reaction.

A new in vitro flow system was developed to investigate the impact of laminar flow on extracellular matrix formation and tissue development. The dynamic in vitro system was designed to provide a cross flow arrangement of main flow induced by a dialysis roller pump (500 ml/min), and nutrition flow by a perfusion pump (3 ml/hr). Poly-L-lysine precoated polyglycolic acid (PGA) scaffolds (3.14 cm2) were seeded with myofibroblasts of human aortic origin (3.0 x 10(6) cells/ mesh) and incubated for 14 days under static conditions. The tissue was exposed to shear stress over a time period of 14 days (n = 4). The control group was seeded under static conditions (n = 4). To obtain a CO2 independent medium, 25 mM HEPES and 1 mM bicarbonate buffer was supplemented to modified MEM without bicarbonate. Gas samples were collected from the medium, and hydroxyproline assay was performed as a marker of collagen production. The newly developed flow system maintained stable cell culture conditions, with the hydroxyproline concentration significantly higher in group F (p < 0.05). These preliminary experiences with a new in vitro tissue culture system demonstrate the feasibility of using flow induced mechanical stress to enhance extracellular matrix formation.

A crucial factor in tissue engineering of heart valves is the functional and physiologic scaffold design. In our current experiment, we describe a new fabrication technique for heart valve scaffolds, derived from x-ray computed tomography data linked to the rapid prototyping technique of stereolithography. To recreate the complex anatomic structure of a human pulmonary and aortic homograft, we have used stereolithographic models derived from x-ray computed tomography and specific software (CP, Aachen, Germany). These stereolithographic models were used to generate biocompatible and biodegradable heart valve scaffolds by a thermal processing technique. The scaffold forming polymer was a thermoplastic elastomer, a poly-4-hydroxybutyrate (P4HB) and a polyhydroxyoctanoate (PHOH) (Tepha, Inc., Cambridge, MA). We fabricated one human aortic root scaffold and one pulmonary heart valve scaffold. Analysis of the heart valve included functional testing in a pulsatile bioreactor under subphysiological and supraphysiological flow and pressure conditions. Using stereolithography, we were able to fabricate plastic models with accurate anatomy of a human valvular homograft. Moreover, we fabricated heart valve scaffolds with a physiologic valve design, which included the sinus of Valsalva, and that resembled our reconstructed aortic root and pulmonary valve. One advantage of P4HB and PHOH was the ability to mold a complete trileaflet heart valve scaffold from a stereolithographic model without the need for suturing. The heart valves were tested in a pulsatile bioreactor, and it was noted that the leaflets opened and closed synchronously under subphysiological and supraphysiological flow conditions. Our preliminary results suggest that the reproduction of complex anatomic structures by rapid prototyping techniques may be useful to fabricate custom made polymeric scaffolds for the tissue engineering of heart valves.

Cell attachment to a scaffold is a precondition for the development of bioengineered valves and vascular substitutes. This attachment is generally facilitated by the use of precoating factors, but some can cause toxic or immunologic side effects. Autologous extracellular matrix (ECM) is used as a precoating factor in our study. Ascending aortic tissue was cultured to obtain human myofibroblasts. Autologous ECM was extracted from the same aortic tissue. Poly(glycolic acid) (PGA) scaffolds were precoated with autologous ECM, human serum, or poly-L-lysine; the control group was pretreated with phosphate buffered saline (PBS). Myofibroblasts were seeded onto each scaffold, and the cell attachment was assayed and compared. Compared with the control group, precoating with human serum, poly-L-lysine, and ECM increased number of attached cells by 24%, 53%, and 48%, respectively. Differences between precoating groups were significant (p < 0.01), except for ECM versus poly-L-lysine. Scanning electron microscopy also demonstrated the high degree of cell attachment to the PGA fibers on scaffolds precoated with ECM and poly-L-lysine. Precoating polymeric scaffold with autologous human extracellular matrix is a very effective method of improving cell attachment in cardiovascular tissue engineering without the potential risk of immunologic reactions.

A crucial factor in tissue engineering of heart valves is the type of scaffold material. In the following study, we tested three different biodegradable scaffold materials, polyglycolic acid (PGA), polyhydroxyalkanoate (PHA), and poly-4-hydroxybutyrate (P4HB), as scaffolds for tissue engineering of heart valves. We modified PHA and P4HB by a salt leaching technique to create a porous matrix. We constructed trileaflet heart valve scaffolds from each polymer and tested them in a pulsatile flow bioreactor. In addition, we evaluated the cell attachment to our polymers by creating four tubes of each material (length equals 4 cm; inner diameter, 0.5 cm), seeding each sample with 8,000,000 ovine vascular cells, and incubating the cell-polymer construct for 8 days (37 degrees C and 5% CO2). The seeded vascular constructs were exposed to continuous flow for 1 hour. Analysis of samples included DNA assay before and after flow exposure, 4-hydroxyproline assay, and environmental scanning electron microscopy (ESEM). We fabricated trileaflet heart valve scaffolds from porous PHA and porous P4HB, which opened and closed synchronously in a pulsatile bioreactor. It was not possible to create a functional trileaflet heart valve scaffold from PGA. After seeding and incubating the PGA-, PHA-, and P4HB-tubes, there were significantly (p < 0.001) more cells on PGA compared with PHA and P4HB. There were no significant differences among the materials after flow exposure, but there was a significantly higher collagen content (p < 0.017) on the PGA samples compared with P4HB and PHA. Cell attachment and collagen content was significantly higher on PGA samples compared with PHA and P4HB. However, PHA and P4HB also demonstrate a considerable amount of cell attachment and collagen development and share the major advantage that both materials are thermoplastic, making it possible to mold them into the shape of a functional scaffold for tissue engineering of heart valves.

Creation of an autologous heart valve by tissue engineering offers a promising approach to cardiac surgery. Although we have demonstrated successful formation of native valve analogous tissue in vitro, hemodynamic competence remains a serious problem. The aim of this study was to optimize in vitro formation of collagen as a precondition for mechanical stability of new tissue. Human myofibroblasts were seeded on square sheets of biodegradable scaffolds (control). To stimulate collagen production, one series was cultured with L-ascorbic acid 2-phosphate. In a second series, the seeded scaffolds were subjected to tension by mounting them on a frame. After 4 weeks of culture time, the collagen content of the different series was assessed by hydroxyproline assay. Light and scanning electron microscopy were performed. Hydroxyproline content of the framed scaffolds was 10 times higher than that of the control group (p < 0.05) and 6 times higher than in the unframed scaffolds grown with ascorbic acid (p < 0.05), respectively. Scanning electron microscopy proved extensive formation of solid tissue in the framed samples. These results demonstrate that supplementation of myofibroblast cultures with ascorbic acid, especially if grown on strained scaffolds, significantly increases collagen content, which is crucial for mechanical stability. This concept is a further step toward the creation of a hemodynamically competent autologous heart valve.