Thermal spraying methods are commonly used to regenerate damaged surface or change materials surface properties. One of the newest methods is cold spraying, where coating is deposited of material in the solid state. Therefore shape and size of the powder particles are very important parameters. The article presents the influence of copper powder morphology on mechanical properties of the coatings (adhesion, hardness, Young's modulus) deposited with the Low Pressure Cold Spraying method on the AA1350 aluminium alloy substrate. The coatings were deposited using two commercially available copper powders with spherical and dendritic morphology and granulation of -40+10 µm. The bond strength of coatings was determined with the pull off method, the hardness with the Vickers method at load of 2.94 N, while the Young's modulus through measurement of nanoindentation. Microstructure of the coatings was analysed using the light and scanning electron microscopy (SEM). Shape of the powder influences mechanical properties of the coating significantly. The coatings deposited with dendritic powder had low mechanical properties, hardness of the 81 HV0.3 order and adhesion of about 4 MPa. However changing powder morphology to spherical increased hardness of the coating to 180 HV0.3 and adhesion to 38.5 MPa. [ABSTRACT FROM AUTHOR]

The paper presents the study of microstructure and corrosion resistance of composite coatings (Al+Al2O3 and Cu+Al2O3) deposited by Low Pressure Cold Spraying method (LPCS). The atmospheric corrosion resistance was examined by subjecting the samples to cyclic salt spray and Kesternich test chambers, with NaCl and SO2 atmospheres, respectively. The selected tests allowed reflecting the actual working conditions of the coatings. The analysis showed very satisfactory results for copper coatings. After eighteen cycles, with a total time of 432 hours, the samples show little signs of corrosion. Due to their greater susceptibility to chloride ions, aluminium coatings have significant corrosion losses. [ABSTRACT FROM AUTHOR]

Pearlitic steels containing from some 0,8 to 0,95% C belong to the group of unalloyed steels intended for cold drawing or rolling. One of the problems discussed in literature is cracking of pearlitic steel subjected to plastic working, caused by high brittleness of the lamellar precipitations of hard cementite. This issue is extremely important because it affects significantly reduce fatigue strength. The paper presents proposals to modify the process of heat treatment, results in getting a steel with spheroidal structure characterized by better plastic properties, in order to eliminate this problem. [ABSTRACT FROM AUTHOR]