Search

Seawater-mixed concrete (SWC) is a proposed solution for catering to the needs of developing nations facing extremely severe water stress. Recent research works advocate the feasibility of producing SWC by adding supplementary cementitious materials (SCMs) and alternative reinforcements without reducing the engineering properties of the same. However, limited information is available for optimising the type and amount of SCMs in binary and ternary blended SW-mixed cementitious systems for achieving desirable strength development and early-age hydration. A comprehensive study to understand the evolution of heat of hydration and strength up to 28 days was conducted on 31 binder compositions mixed with both fresh water (FW) and seawater (SW). Fly ash, slag, metakaolin, and limestone are the supplementary cementitious materials used with CEM I as a primary binder at a replacement level between 10 and 70%. Isothermal calorimetry results revealed an increase in total heat of hydration and a reduction in setting time with SW-mixed cement pastes compared to their FW-mixed counterparts. Similarly, a significant increase in strength between 0 and 50% was observed in SW-mixed cement pastes. Suitable binder combinations showing an increase in compressive strength and not a significant reduction in strength compared to the CEM I reference mix were identified using the strength improvement factor approach. Binary and ternary blended cementitious, consisting of fly ash, slag, and metakaolin at different replacement levels, are amongst the chosen binder combinations. [ABSTRACT FROM AUTHOR]

This paper aims to investigate the feasibility of the incorporation of nanosilica (NS) in ultra-lightweight foamed concrete (ULFC), with an oven-dry density of 350 kg/m3, in regard to its fresh and hardened characteristics. The performance of various dosages of NS, up to 10 wt.-%, were examined. In addition, fly ash and silica fume were used as cement replacing materials, to compare their influence on the properties of foamed concrete. Mechanical and physical properties, drying shrinkage and the sorption of concrete were measured. Scanning electron microscopy (SEM) and X-ray microcomputed tomography (µ-CT) and a probabilistic approach were implemented to evaluate the microstructural changes associated with the incorporation of different additives, such as wall thickness and pore anisotropy of produced ULFCs. The experimental results confirmed that the use of NS in optimal dosage is an effective way to improve the stability of foam bubbles in the fresh state. Incorporation of NS decrease the pore anisotropy and allows to produce a foamed concrete with increased wall thickness. As a result more robust and homogenous microstructure is produced which translate to improved mechanical and transport related properties. It was found that replacement of cement with 5 wt.-% and 10 wt.-% NS increase the compressive strength of ULFC by 20% and 25%, respectively, when compared to control concrete. The drying shrinkage of the NS-incorporated mixes was higher than in the control mix at early ages, while decreasing at 28 d. In overall, it was found that NS is more effective than other conventional fine materials in improving the stability of fresh mixture as well as enhancing the strength of foamed concrete and reducing its porosity and sorption. [ABSTRACT FROM AUTHOR]