The effects of annealing on structure and laser-induced damage threshold (LIDT) of Ta2O5/SiO2 dielectric mirrors were investigated. Ta2O5/SiO2 multilayer was prepared by ion beam sputtering (IBS), then annealed in air under the temperature from 100 to 400 °C. Microstructure of the samples was characterized by X-ray diffraction (XRD). Absorption of the multilayer was measured by surface thermal lensing (STL) technique. The laser-induced damage threshold was assessed using 1064 nm free pulsed laser at a pulse length of 220 μs.It was found that the center wavelength shifted to long wavelength gradually as the annealing temperature increased, and kept its non-crystalline structure even after annealing. The absorbance of the reflectors decreased after annealing. A remarkable increase of the laser-induced damage threshold was found when the annealing temperature was above 250 °C. [Copyright &y& Elsevier]

Abstract: HfO2 films were deposited by electron beam evaporation with different deposition parameters. The properties such as refractive index, weak absorption, and laser induced damage thresholds (LIDTs) of these films have been investigated. It was found that when pulsed Nd:YAG 1064nm laser is used to investigate LIDT of films: Metallic character is the main factor that influences LIDTs of films obtained from Hf starting material by ion-assisted reaction, and films prepared with higher momentum transfer parameter P have fewer metallic character; The ion-assisted reaction parameters are key points for preparing high LIDT films and if the parameters are chose properly, high LIDT films can be obtained. [Copyright &y& Elsevier]