Deep oscillation magnetron sputtering (DOMS) is a novel high power impulse magnetron sputtering technique, which offers large voltage oscillation packets to generate a stable high-power discharge plasma with high ionization under virtually arc-free conditions. CrN/TiN superlattice coatings were deposited using a combined DOMS and pulsed dc magnetron sputtering (PDCMS) in a closed field unbalanced magnetron sputtering configuration. The Cr target was powered at 400 W by DOMS and Ti target was powered at 2000 W by PDCMS. The negative substrate bias ( V s ) ranged from 0 V to −100 V. As the V s was increased, CrN/TiN superlattice coatings showed a single phase face-centered cubic structure with a strong (1 1 1) texture. Correspondingly, the coatings exhibited the dense microstructure with well-defined interfaces between CrN and TiN layers. The increase in V s led to a decrease in grain size and an increase in the compressive residual stress. The hardness and Young's modulus of the coatings increased with increasing V s . The H / E * and H 3 / E * 2 ratios and critical loads L C in scratch test showed an initial increase, followed by a decrease. The wear mechanism changed from severe adhesion wear to abrasion wear. The coating deposited at V s = −60 V exhibited mild abrasion wear with the lowest friction coefficient of 0.27 and the lowest specific wear rate of 0.5 × 10 −6 mm 3 N −1 m −1 due to high hardness, H / E * and H 3 / E * 2 ratios, L C1 and L C3 of 36 GPa, 0.094, 0.316, 15.3 N and 24 N, respectively. The coatings also exhibited increasing pitting corrosion resistance with lower current density and higher corrosion potential in 3.5 wt% NaCl aqueous solution. Combined DOMS + PDCMS techniques can provide the engineering surfaces for the industrial applications with the combined improvement in wear and corrosion resistance. [ABSTRACT FROM AUTHOR]

Abstract: Low-pressure oxygen and argon plasmas were used to pre-treat nylon fabrics, and the modified fabrics, together with the raw fabrics, were subsequently coated with single walled carbon nanotubes (SWCNTs) by a dip-drying process. Scanning electron microscopy (SEM) and Raman spectroscopy analyses indicated the attachment of SWCNTs onto nylon fabrics. After the coating with SWCNTs, the plasma modified fabrics exhibited sheet resistance of as low as 2.0kΩ/sq. with respect to 4.9kΩ/sq. of the raw fabrics, presumably owing to the increase of fibre surface roughness incurred by the plasma modification, which is evidenced by SEM analyses. Fourier transform infrared spectroscopy (FTIR) analysis indicates the incorporation of oxygen functionalities on fibre surfaces in the plasma modification. This is responsible for the variation of the electrical conductance of SWCNT-coated fabrics with the type of plasma and the duration of plasma ablation. [Copyright &y& Elsevier]