In the last few years, some advances have been made in the theoretical modelling of ion exchange processes in glass. On the one hand, the equations that describe the evolution of the cation concentration were rewritten in a more rigorous manner. This was made into two theoretical frameworks. In the first one, the self-diffusion coefficients were assumed to be constant, whereas, in the second one, a more realistic cation behaviour was considered by taking into account the so-called mixed ion effect. Along with these equations, the boundary conditions for the usual ion exchange processes from molten salts, silver and copper films and metallic cathodes were accordingly established. On the other hand, the modelling of some ion exchange processes that have attracted a great deal of attention in recent years, including glass poling, electro-diffusion of multivalent metals and the formation/dissolution of silver nanoparticles, has been addressed. In such processes, the usual approximations that are made in ion exchange modelling are not always valid. An overview of the progress made and the remaining challenges in the modelling of these unique processes is provided at the end of this review. [ABSTRACT FROM AUTHOR]

Featured Application: The paper describes a method allowing to control the chemical strengthening of glass by the ion exchange method. Process control is very simple; it comes down to current temperature measurements. The proposed method can find applications in industrial processes. The paper presents the results of tests on stresses produced by the K+↔Na+ ion exchange method in BK7 glass. Diffusion ion exchange processes were carried out in glass plates with a surface area of a few cm2. The duration of these processes ranged from several hours to several hundred hours; process temperatures from 370 to 402 degree Celsius were used. The area of the glass in which the ion exchange took place shows refractive changes which are also accompanied by stresses. The planar waveguides produced in this way were tested by optical methods (for wavelength λ = 677 nm) and the refractive index profiles for the Transverse Electric (TE) and Transverse Magnetic (TM) polarization states were determined. On the basis of elasto-optic constants, the resulting stresses were determined. The temperature characteristics of diffusion coefficients of exchanged ions were also determined. Based on them a numerical simulation of real-time diffusion processes was possible, which allowed to predict the stresses arising in the glass. A good agreement between these predictions and the results of measurements was obtained. [ABSTRACT FROM AUTHOR]