Low resistance non-alloyed ohmic contacts are realized by a metal-first process on homoepitaxial, heavily n+ doped (010) β-Ga2O3. The resulting contacts have a contact resistance (Rc) as low as 0.23 Ω-mm on an as-grown sample and exhibit nearly linear ohmic behavior even without a post-metallization anneal. The metal-first process was applied to form non-alloyed contacts on n+ (010) β-Ga2O3 grown by metal-organic chemical vapor deposition (MOCVD) as well as suboxide molecular beam epitaxy. Identical contacts fabricated on similar MOCVD samples by conventional liftoff processing exhibit highly rectifying Schottky behavior. Re-processing using the metal-first process after removal of the poor contacts by conventional methods does not improve the contacts; however, addition of a Ga-flux polishing step followed by re-processing using a metal-first process again results in low resistance, nearly linear ohmic contacts. The liftoff process, therefore, does not reliably render nearly linear ohmic behavior in non-alloyed contacts. Furthermore, no interface contamination was detected by x-ray photoelectron spectroscopy. This suggests that during the initial liftoff processing, a detrimental layer may form at the interface, likely modification of the Ga2O3 surface, that is not removable during the contact removal process but that can be removed by Ga-flux polishing. [ABSTRACT FROM AUTHOR]

We demonstrated 500 °C operation of field-effect transistors made using ultra-wide bandgap semiconductor β-Ga2O3. Metal–semiconductor field-effect transistors were fabricated using epitaxial conductive films grown on an insulating β-Ga2O3 substrate, TiW refractory metal gates, and Si-implanted source/drain contacts. Devices were characterized in DC mode at different temperatures up to 500 °C in vacuum. These variable-temperature measurements showed a reduction in gate modulation of the drain current due to an increase in gate leakage across the gate/semiconductor Schottky barrier. Devices exhibited a reduction in transconductance with increasing temperature; despite this, drain current increased with temperature due to a reduction in threshold voltage caused by the de-trapping of electrons from deep-level traps. Devices also showed negligible change in semiconductor epitaxy and source/drain contacts, hence demonstrated recovery to their room-temperature electrical properties after the devices were tested intermittently at different high temperatures in vacuum. The mechanism of gate leakage was also explored, which implicated the presence of different conduction mechanisms at different temperatures and gate electric fields. [ABSTRACT FROM AUTHOR]