Recently, Pb(Mg1/3Nb2/3)O3-xPbTiO3 (PMN-xPT) single crystals present tremendous potential in optical applications such as Q-switches and invisible robotic devices because they possess high electro-optic properties and perfect transparency simultaneously. However, due to the difficulties in testing and sample preparation, the nonlinear optical properties of PMN-PT single crystals have not been reported yet, which poses a bottleneck for exploring its nonlinear application. In this work, a large second-order nonlinear coefficient (d31 ∼ 77.9 pm V−1) of single domain PMN-0.39PT single crystal has been revealed, which is times times higher than the maximum nonlinear coefficient of commercial LiNbO3 single crystal (d33 = 25.4 pm V−1). The complete set of nonlinear coefficients of the sample has been determined by second harmonic generation microscopy. This work presents the promising nonlinear optical property in PMN-PT single crystals and opens a door for designing high-performance nonlinear optical devices. [ABSTRACT FROM AUTHOR]

Alternating current polarization (ACP) has been demonstrated to enhance the performance of 1-3 piezoelectric single crystal composites (PSCCs), compared to direct current polarization (DCP). However, the scaling effect and temperature stability of PSCCs under different polarization modes, which are of significance to practical applications, have rarely been studied. Here, we compared and analyzed the thickness and temperature-dependent properties of PSCCs under ACP and DCP. The results indicated that ACP PSCCs have improved piezoelectric, electromechanical coupling, and dielectric properties. There were scaling effects for PSCCs with thickness below 400 μm. Compared to high-thickness PSCCs, the piezoelectric coefficient (d33), free dielectric constant ( ε 33 T ε 0 ) as well as thickness electromechanical coupling factor (kt) of low-thickness samples were inferior and the corresponding performance enhancements under ACP were also relatively low. In contrast, the clamped dielectric constant ( ε 33 S ε 0 ) did not show significant thickness correlation. As for temperature stability, all performances of PSCCs improved with increase in temperature and the performance enhancement with temperature change was not dependent on the polarization conditions. This work provides reference significance of selecting appropriate polarization for PSCCs, thus benefiting the design and preparation for transducers. [ABSTRACT FROM AUTHOR]