Search

Highlights: [•] Novel-structured TiO2/CuO composite nanofibers was optimized for H2 generation. [ • ] Vivid changes of physicochemical properties influenced by calcinations temperature. [ • ] Significance of physicochemical properties synergy on H2 generation was revealed. [ • ] The optimized photocatalyst exhibited the highest H2 generation activity. [ • ] Reusable and stable with negligible Cu leaching. [Copyright &y& Elsevier]

Abstract: Here, hierarchically meso/nanoporous TiO2 was successfully fabricated by a facile and efficient hydrolysis and calcination method using Ti(OC4H9)4 and K2S2O8 as precursors. The hydrosol was firstly prepared by drop-wise adding ethanol dissolved Ti(OC4H9)4 solution into acetone dissolved K2S2O8 solution under a vigorous stirring and heating condition. After being sufficiently hydrolyzed, the hydrosol was calcined to promote the crystallization of TiO2 and successfully dope S and C on TiO2. The calcination temperature significantly affects the doping of S and C on TiO2, crystallization of TiO2, formation of hierarchically meso/nanoporous structure of TiO2 and its light absorption capability. The S- and C-codoped TiO2 exhibits high photocatalytic H2 generation efficiency in a water/methanol sacrificial reagent system under the irradiation of UV light. The high photocatalytic efficiency is dependent on the comprehensively competing effects of the codoping of S and C, crystallization, specific surface area and light absorption capability. The S- and C-codoped TiO2 calcined at 600°C demonstrates the highest photocatalytic H2 generation efficiency, which is ascribed to the balanced synergy of the abovementioned factors. [Copyright &y& Elsevier]

Abstract: Through hydrothermally growing SrTiO3 cubics on the surface of electrospun TiO2 nanofibers, SrTiO3/TiO2 nanofibers heterostructures were successfully fabricated in the present study. This process is able to ensure uniform distribution of SrTiO3 on the surface of TiO2 nanofibers and lead to close contact between SrTiO3 and TiO2, which is beneficial for the fast separation of photogenerated electrons and holes so as to suppress the recombination of photogenerated electrons and holes at the interphase of SrTiO3 and TiO2. Besides this, the long 1D fibrous structure easy for electron transfer, the hierarchical structure promoting mass transfer and allowing more light reflection and absorption, and the large specific surface area providing more reactions sites to facilitate the reactants to desired oxidation places all together create a synergistic effect on improving the photocatalytic activity of the hierarchical SrTiO3/TiO2 nanofibers heterostructures. Under the irradiation of UV light, in a water/methanol sacrificial reagent system, the SrTiO3/TiO2 nanofibers heterostructures generate five times more H2 than bare TiO2 nanofibers because of its high photocatalytic activity. [Copyright &y& Elsevier]

Abstract: Hierarchical porous TiO2 hollow microspheres were synthesized by a facile approach from a one-step template method. This novel approach avoids tedious multiple steps from conventional template method for fabricating hierarchical porous and hollow microspheres. The as-prepared microspheres were characterized by XRD, SEM, TEM, nitrogen adsorption, and UV–vis DRS. Its photocatalytic activity was demonstrated in the photocatalytic degradation of Rhodamine B. Structural characterization indicates that the as-prepared microspheres had a hollow interior and a hierarchical porous structure with both large and small mesopores on its surface. The average diameters and BET surface areas of the hierarchical porous TiO2 hollow microspheres were 1.5μm and 117m2/g, respectively. Optical adsorption investigation shows that the hierarchical porous TiO2 hollow microspheres possessed the optical band gap of 3.42eV. A possible formation mechanism for the hierarchical porous TiO2 hollow microspheres was discussed. The hierarchical porous TiO2 hollow microspheres exhibited much higher photocatalytic activity than the commercial P25 TiO2. In addition, the as-prepared microspheres can be easily recycling for reuse. All these advantages show a bright future for this microspheric photocatalyst in environmental purification. [Copyright &y& Elsevier]

Abstract: Here we present a simple two-phase assembling method to produce high-quality graphene oxide–TiO2 nanorod composites (GO–TiO2 NRCs) on gram scale. TiO2 nanorods dispersed in toluene are synthesized from a facile two-phase hydrothermal method. The effective attachment of TiO2 nanorods on the whole GO sheets at the water–toluene interface is confirmed by Transmission Electron Microscope (TEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). The as-synthesized TiO2 nanorods show a slightly higher efficiency in the photocatalytic degradation of C. I. Acid Orange 7 (AO 7) irradiated under UV light (λ =254nm) and higher antibacterial activity under simulated sunlight than that of TiO2 nanoparticles with the same diameter. After combined with graphene oxide (GO), the GO–TiO2 NRCs show much higher photocatalytic activities than that of TiO2 nanorods alone and the GO–TiO2 nanoparticle composites (GO–TiO2 NPCs). The ratio of TiO2 and GO has no evident effect on the photocatalytic activity of GO–TiO2 NRCs when all the TiO2 nanorods are anchored on the GO sheets. The higher photocatalytic activity of GO–TiO2 NRCs is ascribed to the anti-charge recombination and the more (101) facets. Considering the superior photocatalytic activity of GO–TiO2 NRCs and the fact that they can been easily mass-produced, we expect this material may find important applications in environmental engineering and other fields. [Copyright &y& Elsevier]