Gold nanoparticle films (Au(NPF)) functionalized with a range of hydrophobic and hydrophilic thiols were assembled in chemiresistor sensor arrays that were used to differentiate between complex mixtures of analytes in the aqueous phase. A chemiresistor array sampled a simple system of linear alcohols (methanol, ethanol, propan-1-ol, and butan-1-ol) dissolved in water over a range of concentrations. Discriminant analysis confirmed that the response patterns of the array could be used to successfully distinguish between the different alcohol solutions at concentrations above 20 mM for all of the alcohols except methanol, which was distinguished at concentrations above 200 mM. Alcohol solutions more dilute than these concentrations had response patterns that were not consistently recognizable and failed cross validation testing. This defined the approximate limit of discrimination for the system, which was close to the limits of detection for the majority of the individual sensors. Another Au(NPF) chemiresistor array was exposed to, and successfully identified crude oil, diesel, and three varieties of gasoline dissolved in artificial seawater at a fixed concentration. This work is a demonstration that the pattern of responses from an array of differently functionalized Au(NPF) sensors can be used to distinguish analytes in the aqueous phase.

A novel chemiresistor sensor for detection of organic analytes in high-conductivity aqueous electrolyte solution is reported. The chemiresistor sensor is based on thin films of gold nanoparticles capped with a 1-hexanethiol monolayer that is inkjet printed onto a microelectrode. In order for a change in nanoparticle film resistance to be measured, the electronic conduction must preferentially occur through the nanoparticle film rather than through the high-conductivity electrolyte solution. This was achieved by miniaturizing the chemiresistor device such that the double layer capacitance of the electrodes in contact with the electrolyte solution gives rise to a significantly larger impedance compared to the nanoparticle film resistance. This system was shown to be sensitive to simple organics dissolved in an aqueous electrolyte solution. The organic analytes, dissolved in the aqueous solution, partition into the hydrophobic nanoparticle film causing the nanoparticle film to swell, resulting in an increase in the low-frequency impedance of the sensor. An increase in the impedance, at 1 Hz, of the gold nanoparticle chemiresistor on exposure to toluene, dichloromethane, and ethanol dissolved in 1 M KCl solution was demonstrated with detection limits of 0.1, 10, and 3000 ppm, respectively. Titration curves over 3 orders of magnitude could be obtained for analytes such as toluene.