Super teak is a fast grown species of teak (Tectona grandis Linn. f) derived from several clones. This has facilitated plantation rotations as short as 5 years. The main target of conventional plantation teak was initially for high value logs. Young teak wood from plantation forest usually has a small diameter. Moreover, the wood from very young stems is unsuitable for direct utilization, but advance wood processing technology can improve the wood properties of small diameter logs. This study aimed to assess the potential utilization of young super teak for high quality products namely furniture, flooring, and veneer, and assess the possibility of the use of manufacture waste for pulp paper and wood pellets as side products. The evaluation were carried out according to the National Indonesian Standard and other international standard requirements. 18 logs from wet (Bogor) and dry (Magetan) sites representing large, medium, and small diameter classes were collected. According to SNI 01-0608-1989 Timber for Furniture, 5-year-old super teak was suitable for furniture production. Furthermore, according to SNI 7732.1: 2011: Teak Veneer, the super teak was classified as Grade C because of the presence of sapwood, pinholes, tight and lose knots. According to Australian Timber Flooring Association, 5-year-old super teak was classifiesd as soft flooring group, the same group as mature teak & radiata pine. The young super teak was classified as Class Quality/Group II with very low active alkali consumption and low Kappa Number according to Indonesian wood fibre criteria for pulp and paper materials and Association of Pulp and Paper in Brazil. Finally, based on SNI 802: 2014 Wood Pellet, the super teak was recommended as by-products for utilising the wood waste. [ABSTRACT FROM AUTHOR]

Variation of fly ash and pulp paper composition at 110°C for 6 hours was carried out to discern the effect of fly ash and pulp paper addition in papercrete. sixth variations in paper pulp and fly ash composition were employed to perceive the characteristic that occurs in the sample. The papercrete material composition was weighed, mixed until it became homogeneous and then casted in a mold with a size of 18 x 5 x 2 cm3. Papercrete samples were allowed to stand within the mold at room temperature for 24 hours and released from the mold to stand again for the next 24 hours, after which it heated at 110°C for 6 hours. Characterization using XRF, SEM-EDX as well as Mechanical and physical tests carried out after the samples was cold. Papercrete with sample code K6 has the highest flexural strength and density value of 2.03 MPa and 2.4 gr/cm3 while papercrete with sample code K1 has the lowest flexural strength and porosity value of 0.4 MPa and 17.89%. Characterization shows that the chemical composition of the samples was dominated by the oxide compound CaO and SiO2 in papercrete. [ABSTRACT FROM AUTHOR]