In this work, methyl orange (MO) was effectively removed from aqueous solution with the calcined product of hydrothermal synthesized Mg/Fe layered double hydroxide (Mg/Fe-LDH). The structure, composition, morphology and textural properties of the Mg/Fe-LDH before and after adsorption were characterized by X-ray diffraction, Fourier transformation infrared spectroscopy, transmission electron microscopy, nitrogen adsorption apparatus and X-ray photoelectron spectroscopy. It was confirmed that MO had been absorbed by calcined Mg/Fe-LDH which had strong interactions with MO. The adsorption of MO onto the Mg/Fe-LDH was systematically investigated by batch tests. The adsorption capacity of the Mg/Fe-LDH toward MO was found to be 194.9 mg • g−1. Adsorption kinetics and isotherm studies revealed that the adsorption of MO onto Mg/Fe-LDH was a spontaneous and endothermic process. These results indicate that Mg/Fe-LDH is a promising material for the removal of MO.

A UV absorber, p-methycinnamic acid (PMCA), was intercalated into Zn-Al layered double hydroxide (LDH) by calcination recovery. Fourier transform infrared spectroscopy showed that the PMCA anions completely replaced the CO32− anions in the interlayer galleries of Zn-Al-LDH containing PMCA anions (Zn-Al-PMCA-LDH). X-ray diffraction and transmission electron microscopy showed that the interlayer distance increased from 0.78 nm to 1.82 nm after the substitution of PMCA anions for CO32− anions. The similar diffraction angles of the CO32− anion-containing Zn-Al-LDH (Zn-Al-CO32−-LDH) and the Zn-Al-CO32−-LDH/styrene–butadiene–styrene (SBS) modified asphalt implied that the asphalt molecules do not enter into the LDH interlayer galleries to form separated-phase structures. The different diffraction angles of Zn-Al-PMCA-LDH and Zn-Al-PMCA-LDH/SBS modified asphalt indicated that the asphalt molecules penetrated into the LDH interlayer galleries to form an expanded-phase structure. UV-Vis absorbance analyses showed that Zn-Al-PMCA-LDH was better able to block UV light due to the synergistic effects of PMCA and Zn-Al-LDH. Conventional physical tests and atomic force microscopy images of the SBS modified asphalt, Zn-Al-CO32−-LDH/SBS modified asphalt and Zn-Al-PMCA-LDH/SBS modified asphalt before and after UV aging indicated that Zn-Al-PMCA-LDH improved the UV aging resistance of SBS modified asphalts.