Rubber magnetic composites were prepared by incorporation of barium ferrite in constant amount—50 phr into acrylonitrile-butadiene rubber. Dicumyl peroxide as the curing agent was used for cross-linking of rubber magnets alone, or in combination with four different types of co-agents. The main aim was to examine the influence of curing system composition on magnetic and physical-mechanical properties of composites. The cross-link density and the structure of the formed cross-links were investigated too. The results demonstrated that the type and amount of the co-agent had significant influence on cross-link density, which was reflected in typical change of physical-mechanical properties. The tensile strength increased with increasing amount of co-agents, which can be attributed to the improvement of adhesion and compatibility on the interphase filler-rubber due to the presence of co-agents. Magnetic characteristics were found not to be influenced by the curing system composition. The application of peroxide curing systems consisting of organic peroxide and co-agents leads to the preparation of rubber magnets with not only good magnetic properties but also with improved physical-mechanical properties, which could broaden the sphere of their application uses. [ABSTRACT FROM AUTHOR]

Rubber magnetic composites were prepared by incorporation of unmodified and surface modified strontium ferrite into rubber matrices based on NBR and NBR/PVC. Strontium ferrite was dosed to the rubber matrices in concentration scale ranging from 0 to 100 phr. The main goal was to investigate the influence of the type of ferrite on the curing process, physical-mechanical and magnetic properties of composites. The mutual interactions between the filler and rubber matrices were investigated by determination of cross-link density and SEM analysis. The incorporation of magnetic fillers leads to the increase of cross-link density and remanent magnetic induction of composites. Moreover, the improvement of physical-mechanical properties was achieved in dependence on the content of magnetic fillers. Surface modification of ferrite contributed to the enhancement of adhesion on the interphase filler-rubber. It can be stated that ferrite exhibits reinforcing effect in the composite materials and this reinforcing behavior was emphasized with the increase in polarity of the rubber matrix. [ABSTRACT FROM AUTHOR]