Novel biochemically active compact polyelectrolyte complexes (CoPECs) are obtained through a simple coprecipitation and compaction procedure. As shown for the system composed of poly(acrylic acid) (PAA) and poly(allylamine) (PAH) as polyelectrolytes and alkaline phosphatase (ALP) as enzyme, the enzyme can be firmly immobilized into these materials. The ALP not only remains active in these materials, but the matrix also enhances the specific activity of the enzyme while protecting it from deactivation at higher temperature. The presence of the matrix allows fine control and substantial enhancement of reaction rates by varying the salt concentration of the contacting solution or temperature. The excellent reusability, together with the ease of co-immobilizing other useful components, such as magnetic particles, allowing facile handling of the CoPECs, makes these materials interesting candidates for variable scaffolds for the immobilization of enzymes for small- and large-scale enzyme-catalyzed processes. [ABSTRACT FROM AUTHOR]

Durable compact polyelectrolyte complexes (CoPECs) with controlled porosity and mechanical properties are prepared by ultracentrifugation. Because the starting materials, poly(allylamine hydrochloride) (PAH) and poly(acrylic acid sodium salt) (PAA), are weak acids/bases, both composition and morphology are controlled by solution pH. In addition, the nonequilibrium nature of polyelectrolyte complexation can be exploited to provide a range of compositions and porosities under the influence of polyelectrolyte addition order and speed, and concentration. Confocal microscopy shows these 'saloplastic' materials to be highly porous, where pore formation is attributed to a combination of deswelling of the polyelectrolyte matrix and expansion of small inhomogenities by osmotic pressure. The porosity (15-70%) and the pore size (<5 μm to >70 μm) of these materials can be tuned by adjusting the PAA to PAH ratio, the salt concentration, and the pH. The modulus of these CoPECs depends on the ratio of the two polyelectrolytes, with stoichiometric complexes being the stiffest due to optimized charge pairing, which correlates with maximized crosslinking density. Mechanical properties, pore sizes, and pore density of these materials make them well suited to three dimensional supports for tissue engineering applications. [ABSTRACT FROM AUTHOR]