The development of effective bifunctional catalysts for the oxygen reduction reaction (ORR) and oxygen evolution reaction (OER) is significant for energy conversion systems, such as Li–air batteries, fuel cells, and water splitting technologies. Herein, a Chlorella-derived catalyst with a nestlike framework, composed of bamboolike nanotubes that encapsulate cobalt nanoparticles, has been prepared through a facile pyrolysis process. It achieves perfect bifunctional catalysis both in ORR and OER on a single catalyst. For our optimal catalyst Co/M-Chlorella-900, its ORR half-wave potential is positively shifted by 40 mV compared to that of a commercial Pt/C catalyst, and the overpotential at 10 mA cm–2for the OER is 23 mV lower than that of a commercial IrO2/C catalyst in an alkaline medium. This superior bifunctional catalytic performance is benefited from the simultaneous increase of pyridinic N sites for ORR and graphitic N sites for OER. In addition, N-doped carbon-encapsulated Co nanoparticles improve both ORR and OER performance by forming new active centers. The unique nestlike carbon nanotube framework not only afforded highly dense ORR and OER active sites but also promoted the electron and mass transfer. Our catalyst also displays notable durability during the ORR and OER, making it promising for use in ORR/OER-related energy conversion systems.

A series of ZIF-derived Fe–N codoped carbon materials with a well-defined morphology, high surface area, tunable sizes and porous nanoframe structure was successfully prepared by synthesizing Fe-doped ZIF-8 through the assembly of Zn2+ions with 2-methylimidazole in the presence of iron(III) acetylacetonate, followed by pyrolysis at a high temperature and in an Ar atmosphere. The prepared optimum catalyst materials exhibited excellent activity for the oxygen reduction reaction (ORR) and outstanding durability in both acidic and alkaline solutions. We found that Fe doping during the ZIF-8 synthesis stage was crucial to achieve the materials’ well-defined morphology, tunable size, good particle dispersion, and high performance. XPS revealed that Fe doping greatly enhanced the fractions of graphitic-N and pyridinic-N and decreased the fraction of oxidized-N. We suggest that the porosity and high surface area of the nanoframe structure originated from the metal–organic frameworks, the high dispersion of Fe in the nanoframe, and the enhanced proportions of active N species, all of which were responsible for the materials’ significantly enhanced ORR performance.